Characterization of the austemperability of partially austenitized ductile iron

被引:21
作者
Fernandino, Diego O. [1 ]
Massone, Juan M. [1 ]
Boeri, Roberto E. [1 ]
机构
[1] Natl Univ Mar del Plata, Met Div INTEMA, CONICET, Mar Del Plata, Buenos Aires, Argentina
关键词
Ductile iron; DPADI; Hardenability; Austemperability; Intercritic interval; DUAL MATRIX STRUCTURES; TENSILE PROPERTIES; PHASE STEELS;
D O I
10.1016/j.jmatprotec.2013.05.002
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This study focuses on the characterization of the hardenability and the austemperability of partially austenitized ductile iron melts alloyed with small amounts of Cu, Ni and Mn. The hardenability was studied by using Jominy tests. The results show that the hardenability of partially austenitized ductile iron samples is significantly lower than that found on the fully austenitized samples. The partially austenitized samples do not show an initial plateau of hardness. This behavior can be caused by the presence of ferrite in the matrix before cooling. This ferrite facilitates the epitaxial growth of new ferrite during cooling, which may account for the drop in hardness and the poor hardenability. The austemperability was measured on round bars after austempering in a molten salt bath. The metallographic studies show that full dual phase microstructure could be obtained only at the smaller diameter rods. As the rod diameter becomes larger, pearlite precipitates. The cooling rate for the advent of pearlite precipitation identified in the Jominy hardenability tests was compared with that observed on the austempering treatments, observing a good correlation. It is proposed that the behavior of ductile iron austempered from partial austenitizing temperatures can be predicted with good accuracy by measuring the cooling rate for the onset of pearlite precipitation on Jominy tests. (c) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码:1801 / 1809
页数:9
相关论文
共 10 条
[1]  
[Anonymous], 1990, DUCTILE IRON DATA DE
[2]   Development of a new mixed (ferritic-ausferritic) ductile iron for automotive suspension parts [J].
Aranzabal, J ;
Serramoglia, G ;
Rousière, D .
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2003, 16 (1-3) :185-190
[3]   Influence of chemical composition and holding time on austenite (γ) → ferrite (α) transformation in ductile iron occurring within the intercritical interval [J].
Basso, A. ;
Martinez, R. ;
Sikora, J. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (41) :9884-9889
[4]   The hardenability of austenite with different alloy content and dispersion in dual-phase steels [J].
Demir, B. ;
Erdogan, M. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 208 (1-3) :75-84
[5]   Effect of ausferrite volume fraction and morphology on tensile properties of partially austenitised and austempered ductile irons with dual matrix structures [J].
Kilicli, V. ;
Erdogan, M. .
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2007, 20 (04) :202-214
[6]   Tensile properties of partially austenitised and austempered ductile irons with dual matrix structures [J].
Kilicli, V. ;
Erdogan, M. .
MATERIALS SCIENCE AND TECHNOLOGY, 2006, 22 (08) :919-928
[7]  
Lamont J.L., 1943, IRON AGE, V152, P64
[8]   ETCHING TECHNIQUE FOR MICROALLOYED DUAL-PHASE STEELS [J].
LAWSON, RD ;
MATLOCK, DK ;
KRAUSS, G .
METALLOGRAPHY, 1980, 13 (01) :71-87
[9]  
Sikora J.A., 2006, P 8 INT S SCI PROC C
[10]   Contribution of dual phase (α, G, B) heat treatments to fatigue properties of SG cast irons [J].
Verdu, C ;
Adrien, J ;
Reynaud, A .
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2005, 18 (06) :346-354