An Easy Fabrication Method to Prepare Inexpensive UV-Cured Transparent Silicone Modified Polyacrylate Coatings with Good Adhesion and UV Resistance

UV-curable polyacrylate is widely used in free-radical type UV-cure coating systems, the disadvantages of which including poor thermal stability and UV resistance can be overcome through chemical modification by silicone. However, it is a remarkable fact that the strategies for fabrication UV-cured silicone modified polyacrylates are somewhat complicated and the price of the products may be much expensive than pure UV-cured polyacrylates. In this work, an easy fabrication method to prepare inexpensive UV-cured transparent silicone modified polyacrylate coatings with good adhesion and UV resistance performance was developed from copolymers of acylates and thiol silicone resin by UV initiated thiol-ene click reaction without UV initiator. The striking results with a high application value should be emphasized that when the amount of thiol silicone resin is only one wt.% of the copolymer of acrylates, the UV-cured coatings obtained exhibit fairly good performance. These coatings prepared exhibit transparency higher than 96% (800 nm), adhesion property to glass slides can reach grade 0, pencil hardness can reach 6H, water absorption is less than 0.16%. In particular, it is observed obviously that the silicone modified polyacrylate coatings exhibit better UV resistance performance than the coating prepared with only copolymers of acrylates initiated by UV initiator 1173. It is proved that it is actually an easy fabrication method to prepare inexpensive UV-cured transparent silicone modified polyacrylate coatings with high performance by UV initiated thiol-ene click reaction of copolymers of acylates and thiol silicone resin.