Inclusion Evolution during Modification of Alumina Inclusions by Calcium in Liquid Steel and Deformation during Hot Rolling Process

被引：73

作者：

Zhao, Dongwei ^{[1
]}

Li, Haibo ^{[1
]}

Bao, Chunlin ^{[1
]}

Yang, Jian ^{[2
]}

机构：

[1] Shougang Res Inst Technol, Beijing 100041, Peoples R China

[2] Heibei Shougang Qianan Iron & Steel CO LTD, Qianan 064404, Peoples R China

来源：

ISIJ INTERNATIONAL | 2015年 / 55卷 / 10期

关键词：

Al2O3-CaS based inclusions; formation mechanism; deformation mechanism; Ca treatment; NONMETALLIC INCLUSIONS; ALLOYED STEEL;

D O I：

10.2355/isijinternational.ISIJINT-2015-064

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The formation mechanism of Al2O3-CaS based inclusions in Al-killed steel was studied by industrial trials and thermodynamic calculations of various calcium aluminates and the precipitated CaS. The chemical activities of CaO and Al2O3 of various calcium aluminates were expressed as a function of CaO and Al2O3 content of CaO-Al2O3 inclusions respectively by the third liner fitting equation obtained from different researchers. Massive Al2O3-CaS based inclusions were generated with a decrease of temperature of molten steel and subsequent solute segregation during casting. Based on the shapes of CaS layer, there are two formulations to consider: 1) the crescent-shaped CaS layer surrounded calcium aluminates was generated by reaction between dissolved Al, S and modified calcium aluminates or diffusion of S dissolved in inclusions; 2) the oval shape layer associated with calcium aluminates was generated by collision or adsorption of calcium aluminates and the precipitated CaS. In addition, the deformation mechanism of inclusions with different modification extents and sizes during hot rolling was proposed.

引用

页码：2115 / 2124

页数：10

共 17 条

[11] Transient Inclusion Evolution During Modification of Alumina Inclusions by Calcium in Liquid Steel: Part II. Results and Discussion [J].

Verma, N. ;

Pistorius, Petrus C. ;

Fruehan, Richard J. ;

Potter, Michael ;

Lind, Minna ;

Story, Scott R. .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2011, 42 (04) :720-729

[12] Transient Inclusion Evolution During Modification of Alumina Inclusions by Calcium in Liquid Steel: Part I. Background, Experimental Techniques and Analysis Methods [J].

Verma, Neerav ;

Pistorius, Petrus C. ;

Fruehan, Richard J. ;

Potter, Michael ;

Lind, Minna ;

Story, Scott .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2011, 42 (04) :711-719

[13] CONTROL OF STRING SHAPED NON-METALLIC INCLUSIONS OF CaO-Al2O3 SYSTEM IN X80 PIPELINE STEEL PLATES [J].

Wang Xinhua ;

Li Xiugang ;

Li Qiang ;

Huang Fuxiang ;

Li Haibo ;

Yang Jian .

ACTA METALLURGICA SINICA, 2013, 49 (05) :553-561

[14] Formation of CaS on Al2O3-CaO inclusions during solidification of steels [J].

Wang, Y ;

Valdez, M ;

Sridhar, S .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2002, 33 (04) :625-632

[15] Formation and Modification of MgO•Al2O3-Based Inclusions in Alloy Steels [J].

Yang, Shufeng ;

Wang, Qiangqiang ;

Zhang, Lifeng ;

Li, Jingshe ;

Peaslee, Kent .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2012, 43 (04) :731-750

[16] Characteristics of Inclusions in Low Carbon Al-Killed Steel during Ladle Furnace Refining and Calcium Treatment [J].

Yang, Wen ;

Zhang, Lifeng ;

Wang, Xinhua ;

Ren, Ying ;

Liu, Xuefeng ;

Shan, Qinglin .

ISIJ INTERNATIONAL, 2013, 53 (08) :1401-1410

[17]

Ye G., 1996, ISIJ International, V36, P105, DOI [10.2355/ISIJINTERNATIONAL.36.SUPPLS105, DOI 10.2355/ISIJINTERNATIONAL.36.SUPPLS105]

← 1 2 →