Effect of preparation conditions on the hydrogen storage capacity of activated carbon adsorbents with super-high specific surface areas

被引：11

作者：

Xie, Hongmei ^{[1
]}

Shen, Yali ^{[1
]}

Zhou, Guilin ^{[1
]}

Chen, Shengming ^{[1
]}

Song, Yinghua ^{[1
]}

Ren, Jianmin ^{[1
]}

机构：

[1] Chongqing Technol & Business Univ, Coll Environm & Biol Engn, Chongqing 400067, Peoples R China

来源：

MATERIALS CHEMISTRY AND PHYSICS | 2013年 / 141卷 / 01期

关键词：

Surfaces; Microporous materials; Nanostructures; Desorption; Adsorption; CHEMICAL ACTIVATION; KOH; CARBONIZATION;

D O I：

10.1016/j.matchemphys.2013.04.045

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A series of activated carbon adsorbents with super-high specific surface areas (SHAC) (S-BET >= 2500 m(2) g(-1)) was prepared and used to adsorb storage hydrogen. The results indicated that the structure of activated carbon adsorbents and hydrogen storage capacity are affected by preparation conditions. The influence of preparation conditions on hydrogen storage capacity can be attributed to changes in the structure of the prepared activated carbon adsorbents. The prepared adsorbents had high hydrogen storage capacity, reaching 5.65 wt % and 4.98 wt % when the adsorption temperatures were 0 degrees C and 25 degrees C, respectively, and the pressure was 9.0 MPa. (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：203 / 207

页数：5

共 25 条

[11] THE REACTION-KINETICS OF HYDROGEN STORAGE IN MG2NI [J].

JUNG, WB ;

NAHM, KS ;

LEE, WY .

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1990, 15 (09) :641-648

[12] A large experimental apparatus for measuring thermal conductance of LH2 storage tank insulations [J].

Kamiya, S ;

Onishi, K ;

Kawagoe, E ;

Nishigaki, K .

CRYOGENICS, 2000, 40 (01) :35-44

[13]

Liang W. J., 1995, PETROLEUM CHEM, P286

[14] Understanding chemical reactions between carbons and NaOH and KOH -: An insight into the chemical activation mechanism [J].

Lillo-Ródenas, MA ;

Cazorla-Amorós, D ;

Linares-Solano, A .

CARBON, 2003, 41 (02) :267-275

[15] About reactions occurring during chemical activation with hydroxides [J].

Lillo-Ródenas, MA ;

Juan-Juan, J ;

Cazorla-Amorós, D ;

Linares-Solano, A .

CARBON, 2004, 42 (07) :1371-1375

[16] Effect of pre-carbonization of petroleum cokes on chemical activation process with KOH [J].

Lu, CL ;

Xu, SP ;

Gan, YX ;

Liu, SQ ;

Liu, CH .

CARBON, 2005, 43 (11) :2295-2301

[17]

Meng N., 2005, RENEW ENERGY RESOUR, V119, P35

[18] Liquid hydrogen: Potential, problems, and a proposed research program [J].

Sherif, SA ;

Zeytinoglu, N ;

Veziroglu, TN .

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1997, 22 (07) :683-688

[19] Hydrogen physisorption capacities of mechanically milled activated carbon powders in a H2 atmosphere using a gravimetric method [J].

Shindo, K ;

Kondo, T ;

Sakurai, Y .

JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 379 (1-2) :252-255

[20] Thermodynamic limits on hydrogen storage in sodalite framework materials: a molecular mechanics investigation [J].

van den Berg, AWC ;

Bromley, ST ;

Jansen, JC .

MICROPOROUS AND MESOPOROUS MATERIALS, 2005, 78 (01) :63-71

← 1 2 3 →