Cavitation erosion resistance of low temperature plasma nitrided martensitic stainless steel

被引:45
作者
Espitia, L. A. [1 ]
Varela, L. [1 ]
Pinedo, C. E. [2 ]
Tschiptschin, A. P. [1 ]
机构
[1] Univ Sao Paulo, Met & Mat Engn Dept, BR-05508030 Sao Paulo, Brazil
[2] Heat Tech Technol Heat Treatment & Surface Engn L, BR-08830000 Mogi Das Cruzes, SP, Brazil
基金
巴西圣保罗研究基金会;
关键词
Low temperature plasma nitriding; Martensitic stainless steel; Expanded martensite; Cavitation erosion; Mechanisms of wear; SLURRY; IMPROVEMENT; STRESS; ALLOY;
D O I
10.1016/j.wear.2012.12.029
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
The cavitation erosion resistance of non-nitrided and low plasma nitrided AISI 410 martensitic stainless steel was evaluated according to ASTM G32 standard. Plasma nitriding was carried out in a hot wall DC-pulsed plasma reactor at 400 degrees C in a mixture of 75% of nitrogen and 25% of hydrogen during 20 h. The ASTM A 743 grade CA6NM stainless steel was used for comparison purposes. The microstructure of the steels was characterized by optical and scanning electron microscopy, as well as by X-ray diffraction. Expanded martensite and iron nitrides were formed at the surface of the martensitic AISI 410 stainless steel. Curves of mass loss, erosion rate and roughness parameters were plotted as a function of exposure time. The 25 mu m thick nitride layer showed two distinct regions: a first 5 mu m thick layer just beneath the surface containing precipitated epsilon Fe3N nitrides and expanded martensite and the rest of the layer constituted solely by expanded martensite. Iron nitride precipitation drastically reduced the incubation period, allowing detachment of entire grains due to the impact of shock-waves over the surface. Despite this, after removal of the first 5 mu m thick layer, the cavitation erosion resistance improved significantly. The relationship between microstructure and time-variation curves and wear mechanisms are discussed. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码:449 / 456
页数:8
相关论文
共 19 条
[1]  
Allenstein A.N., 2007, CAVITATION EROSION R
[2]  
[Anonymous], 1979, 50190 DIN 3
[3]   Simulation of the residual stress development in the diffusion layer of low alloy plasma nitrided steels [J].
Buchhagen, P ;
Bell, T .
COMPUTATIONAL MATERIALS SCIENCE, 1996, 7 (1-2) :228-234
[4]  
Cheng L., 1990, PHASE TRANSFORMATION
[5]   Stress and Composition of Carbon Stabilized Expanded Austenite on Stainless Steel [J].
Christiansen, Thomas L. ;
Somers, Marcel A. J. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (08) :1791-1798
[6]   Friction and rolling-sliding wear of DC-pulsed plasma nitrided AISI 410 martensitic stainless steel [J].
Corengia, P ;
Walther, F ;
Ybarra, G ;
Sommadossi, S ;
Corbari, R ;
Broitman, E .
WEAR, 2006, 260 (4-5) :479-485
[7]   Microstructure and corrosion behaviour of DC-pulsed plasma nitrided AISI 410 martensitic stainless steel [J].
Corengia, P ;
Ybarra, G ;
Moina, C ;
Cabo, A ;
Broitman, E .
SURFACE & COATINGS TECHNOLOGY, 2004, 187 (01) :63-69
[8]   Cavitation erosion resistance of AISI 420 martensitic stainless steel laser-clad with nickel aluminide intermetallic composites and matrix composites with TiC reinforcement [J].
Duraiselvam, Muthukannan ;
Galun, Rolf ;
Wesling, Volker ;
Mordike, Barry L. ;
Reiter, Rolf ;
Oligmueller, Joerg .
SURFACE & COATINGS TECHNOLOGY, 2006, 201 (3-4) :1289-1295
[9]   EBSD and AFM observations of the microstructural changes induced by low temperature plasma carburising on AISI 316 [J].
Gallo, Santiago Corujeira ;
Dong, Hanshan .
APPLIED SURFACE SCIENCE, 2011, 258 (01) :608-613
[10]   Characteristics of martensitic stainless steel nitrided in a low-pressure RF plasma [J].
Kim, SK ;
Yoo, JS ;
Priest, JM ;
Fewell, MP .
SURFACE & COATINGS TECHNOLOGY, 2003, 163 :380-385