Corrosion properties of surface-modified AZ91D magnesium alloy

被引：86

作者：

He Meifeng ^{[1
]}

Liu Lei ^{[1
]}

Wu Yating ^{[1
]}

Tang Zhixin ^{[1
]}

Hu Wenbin ^{[1
]}

机构：

[1] Shanghai Jiao Tong Univ, State Key Lab Metal Matrix Composites, Shanghai 200030, Peoples R China

来源：

CORROSION SCIENCE | 2008年 / 50卷 / 12期

关键词：

Magnesium; Molten salts; Polarization; EIS;

D O I：

10.1016/j.corsci.2008.09.034

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Samples of AZ91D magnesium alloy were dipped into AlCl3-NaCl molten salt at different temperatures between 250 degrees C and 400 degrees C for 28800 s. The thickness of the alloying layer is increased with the rise of the treatment temperatures. The coating was mainly composed of Al12Mg17 and Al3Mg2 intermetallic compounds. The corrosion resistance of the coating which is obtained at 300 degrees C for 28800 s is the best, When the treatment temperature is higher than 300 degrees C, some cracks developed in the alloying layers. The cracks were resulted from the thermal stress due to the different thermal expansion coefficient of the AZ91D substrate and the alloying coating during the rapid cooling process. (C) 2008 Elsevier Ltd. All rights reserved.

引用

页码：3267 / 3273

页数：7

共 38 条

[1] The role of the magnesium industry in protecting the environment [J].

Aghion, E ;

Bronfin, B ;

Eliezer, D .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2001, 117 (03) :381-385

[2]

[Anonymous], 1996, MET FINISH

[3]

Baghni IM, 2004, T NONFERR METAL SOC, V14, P1

[4]

Baghni IM, 2003, T NONFERR METAL SOC, V13, P1253

[5] The corrosion of pure magnesium in aerated and deaerated sodium sulphate solutions [J].

Baril, G ;

Pébère, N .

CORROSION SCIENCE, 2001, 43 (03) :471-484

[6] INFLUENCE OF HOMOGENIZATION AND ARTIFICIAL AGING HEAT-TREATMENTS ON CORROSION BEHAVIOR OF MG-AL ALLOYS [J].

BELDJOUDI, T ;

FIAUD, C ;

ROBBIOLA, L .

CORROSION, 1993, 49 (09) :738-745

[7] Characterisation by EIS of ternary Mg alloys synthesised by mechanical alloying [J].

Brett, CMA ;

Dias, L ;

Trindade, B ;

Fischer, R ;

Mies, S .

ELECTROCHIMICA ACTA, 2006, 51 (8-9) :1752-1760

[8] Conversion-coating treatment for magnesium alloys by a permanganate-phosphate solution [J].

Chong, KZ ;

Shih, TS .

MATERIALS CHEMISTRY AND PHYSICS, 2003, 80 (01) :191-200

[9] Electroless nickel plating of magnesium [J].

Fairweather, WA .

TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 1997, 75 :113-117

[10] Protective coatings on magnesium and its alloys - a critical review [J].

Gray, JE ;

Luan, B .

JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 336 (1-2) :88-113

← 1 2 3 4 →