Microstructure evolution during solution heat treatment of semisolid cast 2024 aluminum alloy

被引：10
作者：
Pannaray, Siriwan [1 ]
Wisutmethangoon, Sirikul [2 ]
Plookphol, Thawatchai [1 ]
Wannasin, Jessada [1 ]
机构：
[1] Prince Songkla Univ, Fac Engn, Dept Min & Mat Engn, Hat Yai 90112, Songkhla, Thailand
[2] Prince Songkla Univ, Fac Engn, Dept Engn Mech, Hat Yai 90112, Thailand
来源：
ADVANCED MANUFACTURING SYSTEMS | 2011年 / 339卷
关键词：
2024 aluminum alloy; solution heat treatment; semisolid;
D O I：
10.4028/www.scientific.net/AMR.339.714
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The aim of this study is to determine the appropriate solution treatment temperature and time of semi solid 2024 Al alloy. Solution heat treatment at 450 degrees C and 480 degrees C for various times, from 4 hours to 16 hrs, were applied followed by artificial aging at 220 degrees C for 1 hr. Microstructure of the semi solid cast 2024 aluminum alloy mainly showed globular grain structure which consisted of matrix-alpha (Al) and grain boundary (GB) - eutectic phases (alpha+Al2CuMg/Al2Cu). Eutectic GB phases was found to completely dissolved after solution heat treatment at 480 C for 14 hrs while sample solution treated at 450 degrees C for the same time showed the existence of remaining GB phases. Prolonging heat treatment after 14 hrs at both temperatures resulted in the formation of coarse black particles at the grain boundaries which were identified as Mg2Si phases. Therefore the suitable solution treatment of the alloy in this study was at 480 degrees C for 14 hrs.
引用
收藏
页码：714 / +
页数：2
相关论文
共 50 条
[31]   Influence of process parameters on microstructure of semisolid A356 alloy slug cast through vertical pipe [J].
Yang Xiao-rong ;
Mao Wei-min ;
Pei Sheng .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (01) :99-103
[32]   Microstructural Evolution of Semisolid 6063 Aluminum Alloy Prepared by Recrystallization and Partial Melting Process [J].
Wang, Yongfei ;
Zhao, Shengdun ;
Zhang, Chenyang .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (09) :4354-4363
[33]   Microstructural Evolution of Semisolid 6063 Aluminum Alloy Prepared by Recrystallization and Partial Melting Process [J].
Yongfei Wang ;
Shengdun Zhao ;
Chenyang Zhang .
Journal of Materials Engineering and Performance, 2017, 26 :4354-4363
[34]   Influence of solution heat treatment on microstructure and hardness of as-cast biodegradable Zn–Mn alloys [J].
Zhang-Zhi Shi ;
Jing Yu ;
Zi-Kai Ji ;
Xue-Feng Liu ;
Xin-Fu Gu ;
Gang Han .
Journal of Materials Science, 2019, 54 :1728-1740
[35]   Microstructure characteristics and mechanical properties of rheoformed wrought aluminum alloy 2024 [J].
郭洪民 ;
杨湘杰 ;
张萌 .
Transactions of Nonferrous Metals Society of China, 2008, (03) :555-561
[36]   Effect of Solution Heat Treatment on Microstructure and Properties of AA7085 Aluminum Alloys [J].
Xiao Daihong ;
Chen Kanghua ;
Luo Weihong .
RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (03) :494-497
[37]   Microstructure characteristics and mechanical properties of rheoformed wrought aluminum alloy 2024 [J].
Guo Hong-min ;
Yang Xiang-jie ;
Zhang Meng .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (03) :555-561
[38]   Semisolid microstructure of Mg2Si/Al composite by cooling slope cast and its evolution during partial remelting process [J].
Qin, Q. D. ;
Zhao, Y. G. ;
Cong, P. J. ;
Zhou, W. ;
Xu, B. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 444 (1-2) :99-103
[39]   Influence of solution heat treatment on localized corrosion of 7A55 aluminum alloy [J].
Zhang, Xin-Ming ;
Wu, Ze-Zheng ;
Liu, Sheng-Dan ;
Feng, Di ;
Ouyang, Hui ;
Wang, Ting .
Cailiao Gongcheng/Journal of Materials Engineering, 2014, (04) :26-33+39
[40]   Effect of Solution Heat Treatment on Microstructure and some Properties of Al–Cu–Mg Alloy [J].
Nikunj Patel ;
Mohit Joshi ;
Abhishek Singh ;
Ajaya Kumar Pradhan .
Transactions of the Indian Institute of Metals, 2023, 76 :2681-2689
12345