Microstructure evolution during solution heat treatment of semisolid cast 2024 aluminum alloy

被引：10
作者：
Pannaray, Siriwan [1 ]
Wisutmethangoon, Sirikul [2 ]
Plookphol, Thawatchai [1 ]
Wannasin, Jessada [1 ]
机构：
[1] Prince Songkla Univ, Fac Engn, Dept Min & Mat Engn, Hat Yai 90112, Songkhla, Thailand
[2] Prince Songkla Univ, Fac Engn, Dept Engn Mech, Hat Yai 90112, Thailand
来源：
ADVANCED MANUFACTURING SYSTEMS | 2011年 / 339卷
关键词：
2024 aluminum alloy; solution heat treatment; semisolid;
D O I：
10.4028/www.scientific.net/AMR.339.714
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The aim of this study is to determine the appropriate solution treatment temperature and time of semi solid 2024 Al alloy. Solution heat treatment at 450 degrees C and 480 degrees C for various times, from 4 hours to 16 hrs, were applied followed by artificial aging at 220 degrees C for 1 hr. Microstructure of the semi solid cast 2024 aluminum alloy mainly showed globular grain structure which consisted of matrix-alpha (Al) and grain boundary (GB) - eutectic phases (alpha+Al2CuMg/Al2Cu). Eutectic GB phases was found to completely dissolved after solution heat treatment at 480 C for 14 hrs while sample solution treated at 450 degrees C for the same time showed the existence of remaining GB phases. Prolonging heat treatment after 14 hrs at both temperatures resulted in the formation of coarse black particles at the grain boundaries which were identified as Mg2Si phases. Therefore the suitable solution treatment of the alloy in this study was at 480 degrees C for 14 hrs.
引用
收藏
页码：714 / +
页数：2
相关论文
共 50 条
[21]   Effects of solution heat treatment on the microstructure, oxidation, and mechanical properties of a cast Ni3Al-based intermetaffic alloy [J].
Lee, DY .
METALS AND MATERIALS INTERNATIONAL, 2006, 12 (02) :153-159
[22]   Microstructure Evolution of Al-Zn-Mg-Cu Alloy by Semisolid Compression [J].
Jiang, Jin ;
Pan, Xinyuan ;
Xu, Shuaikang ;
Liu, Li ;
Zhang, Ke ;
Li, Jinghui ;
Zhang, Mingya .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (19) :10495-10504
[23]   Recrystallization and microstructure evolution of hot extruded 7075 aluminum alloy during semi-solid isothermal treatment [J].
Xiao, Guanfei ;
Jiang, Jufu ;
Liu, Yingze ;
Wang, Ying ;
Guo, Baoyong .
MATERIALS CHARACTERIZATION, 2019, 156
[24]   Effects of cooling rate on solution heat treatment of as-cast A356 alloy [J].
Yang, Chang-lin ;
Li, Yuan-bing ;
Dang, Bo ;
Lue, He-bin ;
Liu, Feng .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2015, 25 (10) :3189-3196
[25]   Localized Recrystallization in Cast Al-Si-Mg Alloy during Solution Heat Treatment: Dilatometric and Calorimetric Studies [J].
S. K. Chaudhury ;
V. Warke ;
S. Shankar ;
D. Apelian .
Metallurgical and Materials Transactions A, 2011, 42 :3160-3169
[26]   Quantitative Microstructure Prediction of Powder High-Temperature Alloy during Solution Heat Treatment and Its Validation [J].
Liu, Zhaofeng ;
Cheng, Junyi ;
Wang, Chao ;
Guo, Jianzheng .
METALS, 2024, 14 (07)
[27]   A study on the re-solution heat treatment of AA 2618 aluminum alloy [J].
Ozbek, Ibrahim .
MATERIALS CHARACTERIZATION, 2007, 58 (03) :312-317
[28]   Microstructural and Mechanical Evolution of Semisolid 7075 Al Alloy Produced by SIMA Process at Various Heat Treatment Parameters [J].
Guner, Ali Tekin ;
Dispinar, Derya ;
Tan, Engin .
ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2019, 44 (02) :1243-1253
[29]   Microstructural and Mechanical Evolution of Semisolid 7075 Al Alloy Produced by SIMA Process at Various Heat Treatment Parameters [J].
Ali Tekin Guner ;
Derya Dispinar ;
Engin Tan .
Arabian Journal for Science and Engineering, 2019, 44 :1243-1253
[30]   Influence of process parameters on microstructure of semisolid A356 alloy slug cast through vertical pipe [J].
杨小容 ;
毛卫民 ;
裴胜 .
Transactions of Nonferrous Metals Society of China, 2008, (01) :99-103
12345