Microstructure evolution during solution heat treatment of semisolid cast 2024 aluminum alloy

被引：10
|
作者：
Pannaray, Siriwan [1 ]
Wisutmethangoon, Sirikul [2 ]
Plookphol, Thawatchai [1 ]
Wannasin, Jessada [1 ]
机构：
[1] Prince Songkla Univ, Fac Engn, Dept Min & Mat Engn, Hat Yai 90112, Songkhla, Thailand
[2] Prince Songkla Univ, Fac Engn, Dept Engn Mech, Hat Yai 90112, Thailand
来源：
ADVANCED MANUFACTURING SYSTEMS | 2011年 / 339卷
关键词：
2024 aluminum alloy; solution heat treatment; semisolid;
D O I：
10.4028/www.scientific.net/AMR.339.714
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The aim of this study is to determine the appropriate solution treatment temperature and time of semi solid 2024 Al alloy. Solution heat treatment at 450 degrees C and 480 degrees C for various times, from 4 hours to 16 hrs, were applied followed by artificial aging at 220 degrees C for 1 hr. Microstructure of the semi solid cast 2024 aluminum alloy mainly showed globular grain structure which consisted of matrix-alpha (Al) and grain boundary (GB) - eutectic phases (alpha+Al2CuMg/Al2Cu). Eutectic GB phases was found to completely dissolved after solution heat treatment at 480 C for 14 hrs while sample solution treated at 450 degrees C for the same time showed the existence of remaining GB phases. Prolonging heat treatment after 14 hrs at both temperatures resulted in the formation of coarse black particles at the grain boundaries which were identified as Mg2Si phases. Therefore the suitable solution treatment of the alloy in this study was at 480 degrees C for 14 hrs.
引用
收藏
页码：714 / +
页数：2
相关论文
共 50 条
  • [1] Semisolid microstructure evolution of the predeformed AZ91D alloy during heat treatment
    Wang, JG
    Lu, P
    Wang, HY
    Liu, JF
    Jiang, QC
    JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 395 (1-2) : 108 - 112
  • [2] Influence of Solution Heat Treatment on Microstructures of Semisolid Cast 7075 Aluminium Alloy
    Mahathaninwong, Narissara
    Wisutmethangoon, Sirikul
    Plookphol, Thawatchai
    Wannasin, Jessada
    ADVANCED MANUFACTURING SYSTEMS, 2011, 339 : 371 - +
  • [3] Microstructure evolution of a novel low-silicon cast aluminum alloy modified with Mn and Cr during solution treatment
    Qian, Dongling
    Lan, Kai
    Yang, Yitao
    MATERIALS CHARACTERIZATION, 2024, 217
  • [4] Microstructure evolution during friction stir welding of 2024 aluminum alloy
    Chang, B. (bhchang@tsinghua.edu.cn), 1600, Harbin Research Institute of Welding (34):
  • [5] Microstructure of as-extruded 7136 aluminum alloy and its evolution during solution treatment
    Yun-Qiang Fan
    Kai Wen
    Zhi-Hui Li
    Xi-Wu Li
    Yong-An Zhang
    Bai-Qing Xiong
    Jian-Xin Xie
    RareMetals, 2017, 36 (04) : 256 - 262
  • [6] Microstructure of as-extruded 7136 aluminum alloy and its evolution during solution treatment
    Fan, Yun-Qiang
    Wen, Kai
    Li, Zhi-Hui
    Li, Xi-Wu
    Zhang, Yong-An
    Xiong, Bai-Qing
    Xie, Jian-Xin
    RARE METALS, 2017, 36 (04) : 256 - 262
  • [7] Microstructure of as-extruded 7136 aluminum alloy and its evolution during solution treatment
    Yun-Qiang Fan
    Kai Wen
    Zhi-Hui Li
    Xi-Wu Li
    Yong-An Zhang
    Bai-Qing Xiong
    Jian-Xin Xie
    Rare Metals, 2017, 36 : 256 - 262
  • [8] Microstructure Evolution of Semisolid Mg-2Zn-0.5Y Alloy during Isothermal Heat Treatment
    Liu Wei
    Yang Doudou
    Quan Gaofeng
    Zhang Yingbo
    Yao Dandan
    RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (08) : 1967 - 1972
  • [9] The Effect of Extrusion and Heat Treatment on the Microstructure and Tensile Properties of 2024 Aluminum Alloy
    Li, Qilun
    Zhang, Xiaobo
    Wang, Lei
    Qiao, Jisen
    MATERIALS, 2022, 15 (21)
  • [10] Research on Semisolid Microstructural Evolution of 2024 Aluminum Alloy Prepared by Powder Thixoforming
    Li, Pubo
    Chen, Tijun
    Zhang, Suqing
    Guan, Renguo
    METALS, 2015, 5 (02): : 547 - 564
12345