Experimental investigation and thermodynamic modeling of the Cu-Ag-Si ternary system

被引:10
作者
Qiu, Chengliang [1 ]
Hu, Biao [1 ]
Zhang, Yu [1 ]
Wang, Xiuyu [1 ]
Wang, Qingping [1 ]
Min, Fanfei [1 ]
Du, Yong [2 ]
机构
[1] Anhui Univ Sci & Technol, Sch Mat Sci & Engn, Huainan 232001, Anhui, Peoples R China
[2] Cent South Univ, State Key Lab Powder Met, Changsha 410083, Hunan, Peoples R China
基金
中国博士后科学基金;
关键词
Thermodynamic modeling; CALPHAD; Cu-Ag-Si system; Phase equilibria; Experiment; REGULAR SOLUTION MODEL; MECHANICAL-PROPERTIES; PHASE-EQUILIBRIA; SILVER-SILICON; ZR; REASSESSMENT; GE; AU;
D O I
10.1016/j.jct.2020.106172
中图分类号
O414.1 [热力学];
学科分类号
摘要
The phase equilibria of the Cu-Ag-Si system were investigated by a combination of key experiments and thermodynamic modeling. Eighteen ternary alloys were prepared to determine the isothermal sections at 500, 600, and 700 degrees C of the Cu-Ag-Si system by means of X-ray diffraction (XRD) and scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM/EDX). The solubilities of Ag in the Cu19Si6, Cu15Si4, Cu56Si11, and hcp(CuSi) phases were measured. No ternary compound was found in this isothermal sections. Based on the experimental equilibria data from the present work, thermodynamic assessment of the Cu-Ag-Si system was carried out by the CALPHAD (CALculation of PHAse Diagrams) approach. The solution phases (Cu), (Ag), (Si), and hcp(CuSi) were described using substitutional solution model and the binary phases Cu19Si6, Cu15Si4, and Cu56Si11 with the solubility of Ag were modeled by the sublattice models. A set of self-consistent thermodynamic parameters of the Cu-Ag-Si system was obtained. The isothermal sections at 500, 600, 650, and 700 degrees C, vertical sections at 10 and 20 at.% Ag, and liquidus projection were calculated. The reaction scheme of the Cu-Ag-Si system was constructed. The calculated results are in agreement with the experimental data from the present work and literature. (c) 2020 Elsevier Ltd.
引用
收藏
页数:11
相关论文
共 40 条
[1]  
[Anonymous], 2007, Computational thermodynamics: The Calphad Method
[2]  
[Anonymous], 1986, Bull. Alloy Phase Diagr, DOI DOI 10.1007/BF02881559
[3]   Silicium-silver alloys [J].
Arrivaut, G .
ZEITSCHRIFT FUR ANORGANISCHE CHEMIE, 1908, 60 (04) :436-440
[4]   Thermodynamic investigation of silver-thallium tellurides by EMF method with solid electrolyte Ag4RbI5 [J].
Babanly, N. B. ;
Orujlu, E. N. ;
Imarnanyeya, S. Z. ;
Yusibov, Y. A. ;
Babanly, M. B. .
JOURNAL OF CHEMICAL THERMODYNAMICS, 2019, 128 :78-86
[5]   ENTHALPY OF FORMATION OF CU-AG-SI (OR GE), AG-AU-SI (OR GE) AND AU-CU-SI (OR GE) LIQUID ALLOYS [J].
CASTANET, R .
JOURNAL OF THE LESS-COMMON METALS, 1988, 136 (02) :287-296
[6]   THERMODYNAMIC EVALUATION OF THE AG-SI SYSTEM [J].
CHEVALIER, PY .
THERMOCHIMICA ACTA, 1988, 130 :33-41
[7]   SGTE DATA FOR PURE ELEMENTS [J].
DINSDALE, AT .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 1991, 15 (04) :317-425
[8]   THE THERMODYNAMICS OF THE LIQUID SOLUTIONS IN THE TRIAD CU-AG-AU .1. THE CU-AG SYSTEM [J].
EDWARDS, RK ;
DOWNING, JH .
JOURNAL OF PHYSICAL CHEMISTRY, 1956, 60 (01) :108-111
[9]  
Gottardi V., 1957, Metall Ital, V49, P721
[10]   Effect of Au Content on Thermal Stability and Mechanical Properties of Au-Cu-Ag-Si Bulk Metallic Glasses [J].
Guo, H. ;
Zhang, W. ;
Chen, M. W. ;
Saotome, Y. ;
Fukuhara, M. ;
Inoue, A. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (06) :1486-1490