Electrochemically deposited cobalt/platinum (Co/Pt) film into porous silicon: Structural investigation and magnetic properties

被引：26

作者：

Harraz, F. A. ^{[1
]}

Salem, A. M. ^{[1
]}

Mohamed, B. A. ^{[2
]}

Kandil, A. ^{[2
]}

Ibrahim, I. A. ^{[1
]}

机构：

[1] CMRDI, Nanostruct Mat & Nanotechnol Div, Cairo 11421, Egypt

[2] Helwan Univ, Dept Chem, Cairo, Egypt

来源：

APPLIED SURFACE SCIENCE | 2013年 / 264卷

关键词：

Porous silicon; Electrochemical deposition; Co/Pt film; Magnetic properties; P-TYPE SILICON; N-TYPE; MACROPORE FORMATION; COPPER; NANOPARTICLES; POLYPYRROLE; MORPHOLOGY; METALS; IRON; COPT;

D O I：

10.1016/j.apsusc.2012.10.032

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

A nanostructured CoPt magnetic film was deposited from a single electrolyte into porous silicon layer by an electrochemical technique, followed by annealing at 600 degrees C in Ar atmosphere during which the CoPt alloy was converted to L1(0) ordered phase. Porous silicon with pore diameter between 5 and 100 nm was firstly fabricated by galvanostatic anodization of n-type silicon wafer in the presence of CrO3 as oxidizing agent and ethanol or sodium lauryl sulfate as surfactants. The role of the surfactant on the produced pore size and morphology was investigated by means of UV-vis spectra. As-formed porous silicon was consequently used as a template for the electrodeposition of magnetic CoPt film. The phase formation, microstructure and the magnetic properties were fully analyzed by XRD, FE-SEM, EDS and VSM measurements. It was found that, upon annealing the coercivity was significantly increased due to the transformation to the L1(0) ordered structure. The saturation magnetization and remanence ratio were also found to increase, indicating no loss of Co content or oxidation reaction after the annealing. Results of synthesis and characterization of CoPt/porous silicon nanocomposite are addressed and thoroughly discussed. (C) 2012 Elsevier B. V. All rights reserved.

引用

页码：391 / 398

页数：8

共 51 条

[41] THE ELECTROCHEMICAL OXIDATION OF SILICON AND FORMATION OF POROUS SILICON IN ACETONITRILE [J].

PROPST, EK ;

KOHL, PA .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (04) :1006-1013

[42]

Rayner-Canham G., 2000, DESCRIPTIVE INORGANI, V2

[43] Microstructural, compositional and magnetic characterization of electrodeposited and annealed Co-Pt-based thin films [J].

Rozman, Kristina Zuzek ;

Kovac, Janez ;

McGuiness, Paul J. ;

Samardzija, Zoran ;

Markoli, Bostjan ;

Kobe, Spomenka .

THIN SOLID FILMS, 2010, 518 (06) :1751-1755

[44] Ferromagnetic nanoparticles embedded in self-arranged matrices [J].

Rumpf, K. ;

Granitzer, P. ;

Poelt, P. ;

Simic, S. ;

Krenn, H. .

PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2008, 205 (06) :1354-1357

[45] Electrochemical stabilization of porous silicon multilayers for sensing various chemical compounds [J].

Salem, M. S. ;

Sailor, M. J. ;

Harraz, F. A. ;

Sakka, T. ;

Ogata, Y. H. .

JOURNAL OF APPLIED PHYSICS, 2006, 100 (08)

[46] Sensing of chemical vapor using a porous multilayer prepared from lightly doped silicon [J].

Salem, M. S. ;

Sailor, M. J. ;

Harraz, F. A. ;

Sakka, T. ;

Ogata, Y. H. .

PHYSICA STATUS SOLIDI C - CURRENT TOPICS IN SOLID STATE PHYSICS, VOL 4 NO 6, 2007, 4 (06) :2073-+

[47] POROUS SILICON MEMBRANES [J].

SEARSON, PC .

APPLIED PHYSICS LETTERS, 1991, 59 (07) :832-833

[48] ELECTROLUMINESCENCE FROM POROUS SILICON AFTER METAL-DEPOSITION INTO THE PORES [J].

STEINER, P ;

KOZLOWSKI, F ;

LANG, W .

THIN SOLID FILMS, 1995, 255 (1-2) :49-51

[49] POROUS SILICON MEMBRANES FOR GAS-SENSOR APPLICATIONS [J].

TALIERCIO, T ;

DILHAN, M ;

MASSONE, E ;

FOUCARAN, A ;

GUE, AM ;

BRETAGNON, T ;

FRAISSE, B ;

MONTES, L .

SENSORS AND ACTUATORS A-PHYSICAL, 1995, 46 (1-3) :43-46

[50] LUMINESCENCE DEGRADATION IN POROUS SILICON [J].

TISCHLER, MA ;

COLLINS, RT ;

STATHIS, JH ;

TSANG, JC .

APPLIED PHYSICS LETTERS, 1992, 60 (05) :639-641

← 1 2 3 4 5 6 →