Phase Evolution upon Aging of Air Plasma Sprayed t'-Zirconia Coatings: II-Microstructure Evolution

被引:72
作者
Krogstad, Jessica A. [1 ]
Leckie, Rafael M. [1 ]
Kraemer, Stephan [1 ]
Cairney, Julie M. [2 ]
Lipkin, Don M. [3 ]
Johnson, Curtis A. [3 ]
Levi, Carlos G. [1 ]
机构
[1] Univ Calif Santa Barbara, Dept Mat, Santa Barbara, CA 93106 USA
[2] Univ Sydney, Australian Ctr Microscopy & Microanal, Sydney, NSW 2006, Australia
[3] GE Global Res, Niskayuna, NY USA
基金
美国国家科学基金会;
关键词
YTTRIA-STABILIZED ZIRCONIA; CUBIC->TETRAGONAL TRANSFORMATION; ZRO2-Y2O3; SYSTEM; TETRAGONAL PHASE; IMPURITY CONTENT; SOLID-SOLUTIONS; ZRO2; TEMPERATURE; PARAMETERS; KINETICS;
D O I
10.1111/j.1551-2916.2012.05460.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The correlation between microstructural and phase evolution in aged, yttria-partially-stabilized zirconia, air plasma-sprayed coatings is discussed. Freestanding coatings with the dense, vertically cracked structure were isothermally aged at 1482 degrees C (2700 degrees F) in air. Characterization of the resulting microstructures was conducted using transmission electron microscopy, then compared with a parallel analysis of the phase evolution via synchrotron X-ray diffraction (XRD) described in Part I. Additional context was provided by related studies on vapor-deposited coatings. Several salient points can be extracted from these assessments. XRD was further validated as a practical method for studying phase stability after clarification of how the possible phases are defined, including the following: (i) the nature of the t' phase observed in XRD after phase decomposition has begun and (ii) the relationship between the Y-rich tetragonal (t?) and Y-rich cubic (c) phases reported to coexist via XRD. A strong relationship between the initial microstructure and the subsequent phase destabilization is also reported. As a result, phase evolution is proposed to proceed via two competing routes. The interplay between these mechanisms dictates the incubation time for monoclinic formation within a given coating.
引用
收藏
页码:299 / 307
页数:9
相关论文
共 33 条
[1]   STRUCTURE AND IONIC MOBILITY OF ZIRCONIA AT HIGH-TEMPERATURE [J].
ALDEBERT, P ;
TRAVERSE, JP .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1985, 68 (01) :34-40
[2]   Phase stability of thermal barrier oxides:: A comparative study of Y and Yb additions [J].
Cairney, Julie M. ;
Rebollo, Noemi R. ;
Ruehle, Manfred ;
Levi, Carlos G. .
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2007, 98 (12) :1177-1187
[3]   The influence of oxides on the performance of advanced gas turbines [J].
Evans, A. G. ;
Clarke, D. R. ;
Levi, C. G. .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2008, 28 (07) :1405-1419
[4]   Phase equilibria and thermodynamic properties of the ZrO2-GdO1.5-YO1.5 system [J].
Fabrichnaya, O ;
Wang, C ;
Zinkevich, M ;
Levi, CG ;
Aldinger, F .
JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2005, 26 (06) :591-604
[5]   Transformation toughening in zirconia-containing ceramics [J].
Hannink, RHJ ;
Kelly, PM ;
Muddle, BC .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (03) :461-487
[6]  
Heuer A.H., 1988, Science and Technology of Zirconia III, V24, P1
[7]  
Heuer A. H., 1984, SCI TECHNOLOGY ZIRCO, P118
[8]   THE DISPLACIVE CUBIC-]TETRAGONAL TRANSFORMATION IN ZRO2 ALLOYS [J].
HEUER, AH ;
CHAIM, R ;
LANTERI, V .
ACTA METALLURGICA, 1987, 35 (03) :661-666
[9]  
HEUER AH, 1988, J AM CERAM SOC, V71, pC170, DOI 10.1111/j.1151-2916.1988.tb05045.x
[10]  
HEUER AH, 1984, SCI TECHNOLOGY ZIRCO, V2, P1