The influence of e-beam irradiation on the morphology and functional properties of UHMWPE

The paper presents an analysis of the effectiveness of radiation modification of GUR 1050 and GUR 1020 polymers intended for endoprosthesis bearing components. It has been demonstrated through extraction and expansion that the crosslinking density increases as the applied dose of electron irradiation and the molecular weight of polyethylene grow. The recorded changes were accompanied by an increase in the degree of crystallinity, which was more significant in the case of the more heavy GUR 1050 (compared to GUR 1020). The morphological changes are supported by the results of micromechanical, sclerometric and tribological examinations. Tribological examinations were documented with SEM images of the surface of specimens subjected to oscillatory friction (roll-block tester). Series of crosswise valleys and projections, arranged along the friction direction, were found on the friction surface. The smoothening of the surface and a lack of lamella fragments on the base specimens which were not subjected to e-beam irradiation are observed along with a reduction of wear due to the increasing dose of irradiation.