Characteristics of the Ti1.27Fe+11 wt.% Ni Composite Obtained by Arc Melting and Ball Milling

被引:1
作者
Bonifacio-Martinez, J. [1 ,2 ]
Urena-Nunez, F. [1 ,3 ]
Iturbe-Garcia, J. L. [2 ]
机构
[1] Univ Autonoma Estado Mexico, Fac Quim, Toluca 50120, Mex, Mexico
[2] Inst Nacl Invest Nucl, Dept Quim, Ocoyoacac 52750, Mex, Mexico
[3] Inst Nacl Invest Nucl, Dept Fis, Ocoyoacac 52750, Mex, Mexico
关键词
HYDROGEN ABSORPTION; FE-TI; NANOCRYSTALLINE; PALLADIUM; TITANIUM; KINETICS; PHASE;
D O I
10.1155/2013/831853
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
The Ti1.27Fe + 11 wt.% Ni composite synthesized by arc melting and ball milling and its possible use in hydrogen storage were studied. First the intermetallic Ti1.27Fe was obtained from elemental powders of Ti and Fe by using the arc melting in argon atmosphere and was cracked in a reactor, after that nickel powder was added to the Ti1.27Fe alloy before the milling. The mixture was subjected to high-energy ball milling to produce the Ti1.27Fe/Ni composite. Nanocrystalline phases Ti1.27Fe + Ni were observed after 5 h of milling. Hydrogenation results indicated that in the first cycle of hydriding the maximum amount of hydrogen release was 2.10 wt.% for the composite at 100 degrees C, under hydrogen pressure of 0.8 MPa and without prior activation.
引用
收藏
页数:5
相关论文
共 20 条
[1]   Hydrogen absorption of TiFe alloy synthesized by ball milling and post-annealing [J].
Abe, M. ;
Kuji, T. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 446 :200-203
[2]   EFFECT OF BALL-MILLING ON THE HYDROGEN ABSORPTION RATE OF FETI AND MG2NI COMPOUNDS [J].
AOKI, K ;
AOYAGI, H ;
MEMEZAWA, A ;
MASUMOTO, T .
JOURNAL OF ALLOYS AND COMPOUNDS, 1994, 203 (1-2) :L7-L9
[3]   HYDROGEN ABSORPTION AND DESORPTION-KINETICS OF TIFE0.8NI0.2H [J].
BERSHADSKY, E ;
KLYUCH, A ;
RON, M .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1995, 20 (01) :29-33
[4]  
Bonifacio-Martinez J., 2002, GERENCIAS CIENCIAS B, P1
[5]   Effect of nickel alloying by using ball milling on the hydrogen absorption properties of TiFe [J].
Bououdina, M ;
Fruchart, D ;
Jacquet, S ;
Pontonnier, L ;
Soubeyroux, JL .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1999, 24 (09) :885-890
[6]   Hydrogenation of TiFe by high-energy ball milling [J].
Chiang, CH ;
Chin, ZH ;
Perng, TP .
JOURNAL OF ALLOYS AND COMPOUNDS, 2000, 307 (307) :259-265
[7]   EFFECT OF SUBSTITUTION OF TITANIUM BY ZIRCONIUM IN TIFE ON HYDROGENATION PROPERTIES [J].
JANG, TH ;
HAN, JI ;
LEE, JY .
JOURNAL OF THE LESS-COMMON METALS, 1986, 119 (02) :237-246
[8]   Nickel-metal hydride battery using nanocrystalline TiFe-type hydrogen storage alloys [J].
Jankowska, E ;
Makowiecka, M ;
Jurczyk, M .
JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 404 :691-693
[9]  
Joint Committee on Powder Diffraction Standards, 1968, PENNS NONPR
[10]   HYDRIDING CHARACTERISTICS OF PALLADIUM AND PLATINUM ALLOYED FETI [J].
KULSHRESHTHA, SK ;
JAYAKUMAR, OD ;
BHATT, KB .
JOURNAL OF MATERIALS SCIENCE, 1993, 28 (15) :4229-4233