Geometrically necessary dislocation density measurements associated with different angles of indentations

被引:67
作者
Dahlberg, C. V. O. [1 ]
Saito, Y. [1 ]
Oztop, M. S. [1 ]
Kysar, J. W. [1 ]
机构
[1] Columbia Univ, Fu Fdn Sch Engn & Appl Sci, Dept Mech Engn, New York, NY 10027 USA
基金
美国国家科学基金会;
关键词
Geometrically necessary dislocation density; Indentation; Single crystal plasticity; Electron backscatter diffraction; IDEALLY PLASTIC CRYSTALS; DUCTILE SINGLE-CRYSTALS; CENTERED-CUBIC CRYSTALS; CRACK-TIP; STRAIN LOCALIZATION; WEDGE INDENTATION; SIMULATIONS; COPPER; EBSD; NANOINDENTATIONS;
D O I
10.1016/j.ijplas.2013.08.008
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Experiments and numerical simulations of various angles of wedge indenters into face-centered cubic single crystal were performed under plane strain conditions. In the experiments, the included angles of indenters are chosen to be 60 degrees, 90 degrees and 120 degrees and they are indented into nickel single crystal into the < 00 (1) over bar > direction with its tip parallel to < 1 1 0 > direction, so that there are three effective in-plane slip systems on (1 1 0) plane. Indenters are applied 200 mu m in depth. The midsection of the specimens is exposed with a wire Electrical Discharge Machining (EDM) and the in-plane lattice rotations of the region around the indented area are calculated from the crystallographic orientation maps obtained from electron backscatter diffraction (EBSD) measurement. No matter which angles of indenters are applied, the rotation fields are very similar. There is a strong lattice rotation discontinuity on the line below the indenter tip. The magnitude of the lattice rotation ranges from -20 degrees to 20 degrees. Lower bounds on the Geometrically Necessary Dislocation (GND) densities are also calculated and plotted. The numerical simulations of the same experimental setup are performed. The simulation results of lattice rotation and slip rates are plotted and compared with the experimental result. There is high correlation between the experimental result and the numerical result. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码:81 / 95
页数:15
相关论文
共 40 条
  • [31] The deformation-induced zone below large and shallow nanoindentations: A comparative study using EBSD and TEM
    Rester, M.
    Motz, C.
    Pippan, R.
    [J]. PHILOSOPHICAL MAGAZINE LETTERS, 2008, 88 (12) : 879 - 887
  • [32] TENSILE CRACK TIP FIELDS IN ELASTIC IDEALLY PLASTIC CRYSTALS
    RICE, JR
    [J]. MECHANICS OF MATERIALS, 1987, 6 (04) : 317 - 335
  • [33] ANTIPLANE SHEAR CRACKS IN IDEALLY PLASTIC CRYSTALS
    RICE, JR
    NIKOLIC, R
    [J]. JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1985, 33 (06) : 595 - 622
  • [34] Wedge indentation into elastic-plastic single crystals, 1: Asymptotic fields for nearly-flat wedge
    Saito, Y.
    Kysar, J. W.
    [J]. INTERNATIONAL JOURNAL OF PLASTICITY, 2011, 27 (10) : 1640 - 1657
  • [35] Wedge indentation into elastic-plastic single crystals. 2: Simulations for face-centered cubic crystals
    Saito, Yuki
    Oztop, Muin S.
    Kysar, Jeffrey W.
    [J]. INTERNATIONAL JOURNAL OF PLASTICITY, 2012, 28 (01) : 70 - 87
  • [36] SIMULIA, 2009, ABAQUS 6 7 US MAN
  • [37] Observations of lattice curvature near the interface of a deformed aluminium bicrystal
    Sun, S
    Adams, BL
    King, WE
    [J]. PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 2000, 80 (01): : 9 - 25
  • [38] The weighted Burgers vector: a new quantity for constraining dislocation densities and types using electron backscatter diffraction on 2D sections through crystalline materials
    Wheeler, J.
    Mariani, E.
    Piazolo, S.
    Prior, D. J.
    Trimby, P.
    Drury, M. R.
    [J]. JOURNAL OF MICROSCOPY, 2009, 233 (03) : 482 - 494
  • [39] On the origin of deformation-induced rotation patterns below nanoindents
    Zaafarani, N.
    Raabe, D.
    Roters, F.
    Zaefferer, S.
    [J]. ACTA MATERIALIA, 2008, 56 (01) : 31 - 42
  • [40] Three-dimensional investigation of the texture and microstructure below a nanoindent in a Cu single crystal using 3D EBSD and crystal plasticity finite element simulations
    Zaafarani, N
    Raabe, D
    Singh, RN
    Roters, F
    Zaefferer, S
    [J]. ACTA MATERIALIA, 2006, 54 (07) : 1863 - 1876