Effects of Cr contents in Fe-based bulk metallic glasses on the glass forming ability and the corrosion resistance

被引:82
作者
Wang, S. L. [1 ]
Li, H. X. [2 ]
Zhang, X. F. [1 ]
Yi, S. [1 ]
机构
[1] Kyungpook Natl Univ, Dept Mat Sci & Met, Taegu 702701, South Korea
[2] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China
关键词
Bulk metallic glass; Glass forming ability; Corrosion resistance; Chromium; AMORPHOUS-ALLOYS; STAINLESS-STEEL; RAW-MATERIALS; HCL SOLUTION; HOT METAL; BEHAVIOR; 304-STAINLESS-STEEL; ENVIRONMENTS; H2SO4;
D O I
10.1016/j.matchemphys.2008.08.057
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Fe-based bulk metallicglasses of Fe69.9-x,C7.1Si3.3B5.5P8.7CrxMo2.5Al2.0Co1.0 (x = 0.0, 2.3-12.3) with high glass forming ability and good corrosion resistance were fabricated using industrial raw materials. Class forming ability of the Fe-based bulk metallic glasses tends to decrease with the Cr content while the corrosion, resistance increases with the Cr content. A homogeneous passive layer on the amorphous sample with 12.3 at% Cr can be formed leading to superior corrosion resistance of the amorphous sample to an austenitic stainless steel (SUS304) in the 0.5 M H2SO4 and 1N HCl solutions at 298 K. Fe-based bulk metallic glasses with an optimum combination of glass forming ability and corrosion resistance can be produced in large quantities through a systematic control of the Cr content for extensive practical applications. (C) 2008 Elsevier B.V. All rights reserved.
引用
收藏
页码:878 / 883
页数:6
相关论文
共 50 条
[21]   Glass-forming Ability and Corrosion Resistance of Zr—Cu—Al—Co Bulk Metallic Glass [J].
W.Zhou ;
W.P.Weng ;
J.X.Hou .
Journal of Materials Science & Technology, 2016, 32 (04) :349-354
[22]   Formation and corrosion properties of Fe-based bulk metallic glasses [J].
Chun-lei Zhu ;
Qing Wang ;
Jie Zhang ;
Ying-min Wang ;
Chuang Dong .
International Journal of Minerals, Metallurgy, and Materials, 2010, 17 :323-326
[24]   Formation and corrosion properties of Fe-based bulk metallic glasses [J].
Zhu, Chun-lei ;
Wang, Qing ;
Zhang, Jie ;
Wang, Ying-min ;
Dong, Chuang .
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2010, 17 (03) :323-326
[25]   Effect of silver on the glass forming ability of MgCuGdY bulk metallic glasses [J].
Soubeyroux, J. L. ;
Puech, S. ;
Blandin, J. J. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 483 (1-2) :107-111
[26]   Acid corrosion process of Fe-based bulk metallic glass [J].
Gostin, P. F. ;
Oswald, S. ;
Schultz, L. ;
Gebert, A. .
CORROSION SCIENCE, 2012, 62 :112-121
[27]   Effect of Industrial Raw Materials on the Glass-Forming Ability, Magnetic and Mechanical Properties of Fe-Based Bulk Metallic Glasses [J].
Yongqian Cai ;
Haibo Ling ;
Tao Jiang .
Metallurgical and Materials Transactions B, 2015, 46 :2484-2489
[28]   Effect of Industrial Raw Materials on the Glass-Forming Ability, Magnetic and Mechanical Properties of Fe-Based Bulk Metallic Glasses [J].
Cai, Yongqian ;
Ling, Haibo ;
Jiang, Tao .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2015, 46 (06) :2484-2489
[29]   Improvement of corrosion resistance in NaOH solution and glass forming ability of as-cast Mg-based bulk metallic glasses by microalloying [J].
Peng Hao1 ;
2.Fundamental Industry Training Center .
China Foundry, 2011, 8 (01) :5-8
[30]   Corrosion performances in simulated body fluids and cytotoxicity evaluation of Fe-based bulk metallic glasses [J].
Wang, Y. B. ;
Li, H. F. ;
Zheng, Y. F. ;
Li, M. .
MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2012, 32 (03) :599-606