High-Jc YBa2CU3O7-x films on metal tapes by the metalorganic deposition method using trifluoroacetates

被引:37
作者
Araki, T
Yuasa, T
Kurosaki, H
Yamada, Y
Hirabayashi, I
Kato, T
Hirayama, T
Iijima, Y
Saito, T
机构
[1] Superconduct Res Lab, Atsuta Ku, Nagoya, Aichi 4568587, Japan
[2] Japan Fine Ceram Ctr, Atsuta Ku, Nagoya, Aichi 4568587, Japan
[3] Fujikura Ltd, Mat Technol Lab, Koto Ku, Tokyo 1358512, Japan
关键词
D O I
10.1088/0953-2048/15/1/101
中图分类号
O59 [应用物理学];
学科分类号
摘要
High-J(c) YBa2Cu3O7-x (YBCO) films on metal tapes have been successfully fabricated by the metalorganic deposition method using trifluoroacetates (TFA-MOD method) with optimal firing conditions. In the firing process, the key factors by which to obtain high-J(c) YBCO films on metal tapes are to prevent the films from deterioration by water vapour and to avoid BaCeO3 creation between YBCO and the CeO2 buffer layer. With the optimal conditions, we have successfully formed a 0.24 mum thick YBCO film on a metal tape, having a J(c) of 2.5 MA cm(-2) (77 K, 0 T).
引用
收藏
页码:L1 / L3
页数:3
相关论文
共 50 条
[41]   Growth of thick YBa2Cu3O7-x films [J].
Hollmann, E.K. ;
Plotkin, D.A. ;
Razumov, S.V. ;
Tumarkin, A.V. .
Physica C: Superconductivity and its Applications, 1998, 296 (1-2) :37-42
[42]   LATTICE MONOCLINIZATION OF YBA2CU3O7-X FILMS [J].
MARTOVITSKY, VP ;
RODIN, VV .
PHYSICA C, 1991, 182 (4-6) :269-276
[43]   THE CHARACTERIZATION OF POTASSIUM DOPED YBA2CU3O7-X CERAMIC TAPES [J].
HAMID, T ;
DEWHUGHES, D ;
SMEETS, A .
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1992, 5 :S308-S311
[44]   The growth of thick YBa2Cu3O7-x films [J].
Hollmann, EK ;
Plotkin, DA ;
Razumov, SV ;
Tumarkin, AV .
PHYSICA C, 1998, 296 (1-2) :37-42
[45]   Edge dislocations in YBa2Cu3O7-x films [J].
Svetchnikov, V .
METALLOFIZIKA I NOVEISHIE TEKHNOLOGII, 1998, 20 (03) :54-58
[46]   Vortex pinning in YBa2Cu3O7-x films [J].
Xenikos, DG ;
Lemberger, TR .
CZECHOSLOVAK JOURNAL OF PHYSICS, 1996, 46 :1653-1654
[47]   TEM STUDY OF YBA2CU3O7-X/MGO/YBA2CU3O7-X TRILAYERS [J].
NAKAJIMA, M ;
MATSUI, M .
PHYSICA C, 1991, 185 :2043-2044
[48]   ISOTROPIC JC-B PROPERTIES OF YBA2CU3O7-X THIN-FILMS CONTAINING FINE PRECIPITATES BY METALORGANIC CHEMICAL VAPOR-DEPOSITION [J].
MATSUNO, S ;
KINOUCHI, S ;
EGAWA, K ;
UMEMURA, T ;
UCHIKAWA, F ;
NAKABAYASHI, S .
APPLIED PHYSICS LETTERS, 1993, 62 (13) :1556-1558
[49]   The characteristics of the YBa2Cu3O7-x thin films on the metal buffer layer [J].
Nishimura, J ;
Yoshida, Y ;
Matsunami, N ;
Takai, Y .
ADVANCES IN SUPERCONDUCTIVITY XII, 2000, :921-923
[50]   GRAIN-GROWTH IN MONOLITHIC YBA2CU3O7 WITH HIGH-JC [J].
MENG, RL ;
SUN, YY ;
HOR, PH ;
CHU, CW .
PHYSICA C, 1991, 179 (1-3) :149-158