Visualization of Damages of the Main Pipelines Using Cyclic Hydro Testing

被引：7

作者：

Student, Oleksandra ^{[1
]}

Krechkovs'ka, Halyna ^{[1
]}

机构：

[1] Natl Acad Sci Ukraine, Karpenko Phisicomech Inst, 5 Naukova Str, UA-79601 Lvov, Ukraine

来源：

21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21) | 2016年 / 2卷

关键词：

pipelines; steel; fractography analysis; damage; fracture; mechanical properties; STEAM PIPELINES; WELDED-JOINTS; POWER-PLANTS; DEGRADATION; STEEL; METAL;

D O I：

10.1016/j.prostr.2016.06.071

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The fracture of the pipelines is often occurred in the vicinity of weld joints. It is important to consider the scattered damages in the bulk material and their effect on the mechanical properties. These damages could be visualized by hydro testing of long-term exploited pipes with following fractography investigation of the obtained fracture surfaces. The bulk damages of 10G2C1 steel after 45 years of operation on the pipeline were analyzed using mechanical characteristics of metal and fractography features of fracture. Strength and ductility characteristics, impact toughness of the exploited steel (as a base metal) and metal from different zones of longitudinal weld joint on the pipe were analyzed. Copyright (C) 2016 The Authors. Published by Elsevier B.V.

引用

页码：549 / 556

页数：8

共 10 条

[1] IN-SERVICE DEGRADATION OF GAS TRUNK PIPELINE X52 STEEL [J].

Gabetta, G. ;

Nykyforchyn, H. M. ;

Lunarska, E. ;

Zonta, P. P. ;

Tsyrulnyk, O. T. ;

Nikiforov, K. ;

Hredil, M. I. ;

Petryna, D. Yu. ;

Vuherer, T. .

MATERIALS SCIENCE, 2008, 44 (01) :104-119

[2]

Hull D., 1999, FRACTOGRAPHY OBSERVI, P340

[3]

Krechkovs'ka H. V., 2015, MAT SCI, V51

[4] Abnormal manifestation of the high-temperature degradation of the weld metal of a low-alloy steel welded joint [J].

Nykyforchyn, H. M. ;

Student, O. Z. ;

Markov, A. D. .

MATERIALS SCIENCE, 2007, 43 (01) :77-84

[5]

Nykyforchyn H.M., 2013, ESIS NEWSLETT, V52, P20

[6] Degradation of welded joints of steam pipelines of thermal electric power plants in hydrogenating media [J].

Nykyforchyn, HM ;

Student, OZ ;

Dzioba, IR ;

Stepanyuk, SM ;

Markov, AD ;

Onyshchak, YD .

MATERIALS SCIENCE, 2004, 40 (06) :836-843

[7] Anisotropy of the Mechanical Properties of Degraded 15Kh1De1F Steel After Its Operation in Steam Pipelines of Thermal Power Plants [J].

Student, D. Z. ;

Krechkovs'ka, H. V. .

MATERIALS SCIENCE, 2012, 47 (05) :590-597

[8] Specific features of the influence of hydrogen on the properties and mechanism of fracture of the metal of welded joints of steam pipelines at thermal power plants [J].

Student, O. Z. ;

Markov, A. D. ;

Nykyforchyn, H. M. .

MATERIALS SCIENCE, 2006, 42 (04) :451-460

[9]

Tsyrul'nyk O. T., MAT SCI, V40, P844

[10] Corrosion and stress-corrosion cracking of exploited storage tank steel [J].

Zagórski A. ;

Matysiak H. ;

Tsyrulnyk O. ;

Zvirko O. ;

Nykyforchyn H. ;

Kurzydłowski K. .

Materials Science, 2004, 40 (3) :421-427

← 1 →