Comparative study of very high cycle tensile and torsional fatigue in TC17 titanium alloy

被引：29
|
作者：
Liu, Hanqing [1 ,2 ]
Wang, Haomin [3 ]
Huang, Zhiyong [1 ,2 ]
Wang, Qingyuan [1 ,2 ]
Chen, Qiang [4 ]
机构：
[1] Sichuan Univ, Minist Educ, Key Lab Energy Engn Safety & Disaster Mech, Chengdu 610065, Peoples R China
[2] Sichuan Univ, Failure Mech & Engn Disaster Prevent & Mitigat Ke, Chengdu 610065, Sichuan, Peoples R China
[3] Chengdu Univ, Inst Adv Study, Chengdu 610106, Peoples R China
[4] Kyushu Univ, Dept Mech Engn, Fukuoka 8190395, Japan
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2020年 / 139卷
基金：
中国国家自然科学基金;
关键词：
Tensile and torsional fatigue; Crack initiation driven force; Very high cycle fatigue; Short crack propagation; FIB; CRACK INITIATION; STRESS RATIO; BEHAVIOR; STEEL; MICROSTRUCTURE; FAILURES; GROWTH; LIFE; DEFORMATION; PROPAGATION;
D O I：
10.1016/j.ijfatigue.2020.105720
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Very high cycle tensile and torsional fatigue of TC17 titanium alloy with bimodal microstructure have been firstly and comparatively studied at the stress ratio of 0.1. Like the tensile cracks, torsional cracks were substantiated to nucleate from specimen surface or interior sites and presented in a fatigue life-dependent mode. Internal tensile and torsional fatigue cracks with faceted morphology were analyzed using focus ion beam and unraveled to initiate in modes II + III that driven by maximum shear stress. Particularly, short crack branching and deflection beneath the crack initiation rough area can be observed for torsional loading condition.
引用
收藏
页数：10
相关论文
共 50 条
  • [41] Effect of shot peening and vibration finishing on the fatigue behavior of TC17 titanium alloy at room and high temperature
    Shi, Hailan
    Liu, Daoxin
    Pan, Yifan
    Zhao, Weidong
    Zhang, Xiaohua
    Ma, Amin
    Liu, Bo
    Hu, Yunhui
    Wang, Wei
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 151
  • [42] Fatigue and anisotropic behavior of wire-arc additive manufactured TC17 titanium alloy
    Yu, Banglong
    Chen, Zhihao
    Wang, Ping
    Liu, Yong
    Song, Xiaoguo
    Dong, Pingsha
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 28 (3463-3474): : 3463 - 3474
  • [43] Quantitative Analysis of the Orientation of Lamellar α in TC17 Titanium Alloy
    Tian Fei
    Zeng Weidong
    Ma Xiong
    Wang Kaixuan
    Shao Yitao
    Zhou Yigang
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (06) : 998 - 1003
  • [44] Crack initiation and early growth behavior of TC4 titanium alloy under high cycle fatigue and very high cycle fatigue
    Li, Wei
    Gao, Ning
    Zhao, Hongqiao
    Xing, Xinxin
    JOURNAL OF MATERIALS RESEARCH, 2018, 33 (08) : 935 - 945
  • [45] Crack initiation and early growth behavior of TC4 titanium alloy under high cycle fatigue and very high cycle fatigue
    Wei Li
    Ning Gao
    Hongqiao Zhao
    Xinxin Xing
    Journal of Materials Research, 2018, 33 : 935 - 945
  • [46] Very High Cycle Fatigue Failure of Near β Titanium Alloy
    E. V. Naydenkin
    A. P. Soldatenkov
    I. P. Mishin
    V. A. Oborin
    A. A. Shanyavskiy
    Physical Mesomechanics, 2021, 24 : 326 - 334
  • [47] Very High Cycle Fatigue Failure of Near β Titanium Alloy
    Naydenkin, E., V
    Soldatenkov, A. P.
    Mishin, I. P.
    Oborin, V. A.
    Shanyavskiy, A. A.
    PHYSICAL MESOMECHANICS, 2021, 24 (03) : 326 - 334
  • [48] Titanium Alloy Materials with Very High Cycle Fatigue: A Review
    Wu, Yuhang
    He, Weifeng
    Ma, Haitao
    Nie, Xiangfan
    Liang, Xiaoqing
    Pan, Jile
    Wang, Shiguang
    Shang, Min
    Cheng, Li
    MATERIALS, 2024, 17 (12)
  • [49] Continuous Cooling Transformation Diagram of TC17 Titanium Alloy
    Cai X.
    Lei M.
    Wan M.
    Zhao F.
    Huang C.
    Wen X.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2019, 43 (12): : 1291 - 1296
  • [50] STUDY ON TENSILE BEHAVIOR OF SiCf/TC17 COMPOSITES
    Zhang Xu
    Wang Yumin
    Yang Qing
    Lei Jiafeng
    Yang Rui
    ACTA METALLURGICA SINICA, 2015, 51 (09) : 1025 - 1037
12345