The influence of reheating temperature and direct-cooling rate after forging on microstructure and mechanical properties of V-microalloyed steel 38MnSiVS5

被引：18

作者：

Dini, Ghasem ^{[1
]}

Vaghefi, Mahmood Monir ^{[1
]}

Shafyei, Ali ^{[1
]}

机构：

[1] Isfahan Univ Technol, Dept Mat Sci & Engn, Esfahan 84154, Iran

来源：

ISIJ INTERNATIONAL | 2006年 / 46卷 / 01期

关键词：

forging; microalloyed steel; strength; toughness;

D O I：

10.2355/isijinternational.46.89

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Wiht the aim of replacing quenched and tempered forging parts and reducing by this way costly and time consuming operations; an industrial forging procedure was developed to evaluate the influence of thermomechanical processing parameters on the microstructure and mechanical properties of vanadium microalloyed steel. In order to study the influence of reheating temperature, after determining the dissolving temperature of vanadium carbonitrides precipitates, samples were heating in temperature rang 1 000 to 1 200 degrees C. After austenitization at 1 100 degrees C, the microalloyed steel billets were forged in a hydraulic press and then cooled with different cooling rates. The metallography and mechanical testing results indicated that by increasing the reheating temperature, the strength and toughness of V-microalloyed steel have not change significantly and so the temperature of 1 200 degrees C was selected for forging. By increasing cooling rate, both strength and toughness improve.

引用

页码：89 / 92

页数：4

共 14 条

[1]

Abad R., 1996, P C FUND APPL MICR F, P284

[2]

Bai DQ, 2001, ISS MWSP CONF P, V39, P543

[3] Fracture behaviour in medium-carbon Ti-V-N and V-N microalloyed ferritic-pearlitic and bainitic forging steels with enhanced machinability [J].