Rapid Determination of Fretting Fatigue Limit by Infrared Thermography

被引：5
作者：
Chhith, S. [1 ,2 ]
De Waele, W. [1 ]
De Baets, P. [1 ,2 ]
机构：
[1] Univ Ghent, Dept Elect Energy Met Mech Construct & Syst, Soete Lab, Technol Pk 903, B-9052 Ghent, Belgium
[2] Flanders Make, Strateg Res Ctr Mfg Ind, Ghent, Belgium
来源：
EXPERIMENTAL MECHANICS | 2018年 / 58卷 / 02期
关键词：
Fatigue limit; Fretting fatigue; Thermography; Fast Fourier Transform; Second harmonic; CRACK INITIATION; BEHAVIOR; DAMAGE; METHODOLOGY; PREDICTION; COMPONENTS; FAILURE;
D O I：
10.1007/s11340-017-0340-9
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This paper demonstrates the feasibility of infrared thermography to determine the so-called fretting fatigue limit. Fretting fatigue tests are performed on aluminum and steel specimens. The coupled fatigue and tangential loads are sequentially increased (block loading) whilst the normal load is kept constant for all blocks. The temperature data is processed and analyzed using a Fast Fourier Transform (FFT) algorithm implemented in the commercial software Matlab. It is demonstrated that the second harmonic of the temperature signal can be linked to the specific loading block below which no or negligible damage is generated in the specimen. The stress amplitude of this block is considered to be a best estimate of the fretting fatigue limit. A constant amplitude fretting fatigue test with this stress amplitude confirmed that the specimen remains intact at 10(7) cycles.
引用
收藏
页码：259 / 267
页数：9
相关论文
共 35 条
[1]   Analysis of pad size effects in fretting fatigue using short crack arrest methodologies [J].
Araújo, JA ;
Nowell, D .
INTERNATIONAL JOURNAL OF FATIGUE, 1999, 21 (09) :947-956
[2]   Fretting fatigue and wear damage of structural components in nuclear power stations - Fitness for service and life management perspective [J].
Attia, M. Helmi .
TRIBOLOGY INTERNATIONAL, 2006, 39 (10) :1294-1304
[3]   Thermomechanical behavior of PA6.6 composites subjected to low cycle fatigue [J].
Benaarbia, Adil ;
Chrysochoos, Andre ;
Robert, Gilles .
COMPOSITES PART B-ENGINEERING, 2015, 76 :52-64
[4]   Crack nucleation threshold under fretting loading by a thermal method [J].
Berthel, B. ;
Moustafa, A. -R. ;
Charkaluk, E. ;
Fouvry, S. .
TRIBOLOGY INTERNATIONAL, 2014, 76 :35-44
[5]   Calorimetric analysis of dissipative and thermoelastic effects associated with the fatigue behavior of steels [J].
Boulanger, T ;
Chrysochoos, A ;
Mabru, C ;
Galtier, A .
INTERNATIONAL JOURNAL OF FATIGUE, 2004, 26 (03) :221-229
[6]   Lock-In Thermography:: A tool to analyse and locate thermo-mechanical mechanisms in materials and structures [J].
Brémond, P ;
Potet, P .
THERMOSENSE XXIII, 2001, 4360 :560-566
[7]  
Bremond P, 2004, PHOTONICS SPECTRA
[8]   Characterization of the mechanical dissipation in shape-memory alloys during stress-induced phase transformation [J].
Bubulinca, C. ;
Balandraud, X. ;
Grediac, M. ;
Stanciu, S. ;
Abrudeanu, M. .
JOURNAL OF MATERIALS SCIENCE, 2014, 49 (02) :701-709
[9]   On-line detection of fretting fatigue crack initiation by lock-in thermography [J].
Chhith, Saosometh ;
De Waele, Wim ;
De Baets, Patrick ;
Van Hecke, Tanja .
TRIBOLOGY INTERNATIONAL, 2017, 108 :150-155
[10]   Static and fatigue characterisation of new basalt fibre reinforced composites [J].
Colombo, C. ;
Vergani, L. ;
Burman, M. .
COMPOSITE STRUCTURES, 2012, 94 (03) :1165-1174
1234