Numerical Modeling of the Development of Intermetallic Layers between Aluminium and Steel during Co-Extrusion

被引：4

作者：

Behrens, B. -A. ^{[1
]}

Klose, C. ^{[2
]}

Thuerer, S. E. ^{[2
]}

Heimes, N. ^{[1
]}

Uhe, J. ^{[1
]}

机构：

[1] Leibniz Univ Hannover, Inst Umformtech & Umformmaschinen Forming Technol, Univ 2, D-30823 Hannover, Germany

[2] Leibniz Univ Hannover, Inst Werkstoffkunde Mat Sci, Univ 2, D-30823 Hannover, Germany

来源：

PROCEEDINGS OF THE 22ND INTERNATIONAL ESAFORM CONFERENCE ON MATERIAL FORMING (ESAFORM 2019) | 2019年 / 2113卷

关键词：

D O I：

10.1063/1.5112563

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Undergoing the Tailored Forming process chain, coaxial aluminium-steel profiles joined by co-extrusion are formed into hybrid bearing bushings by die forging. During the joining of aluminium and steel, intermetallic phases may develop. As these phases are very hard and brittle, it is important to be able to predict the width of the resulting intermetallic layer because it is likely to reduce the strength of the compound for the subsequent forging step. In the scope of this paper, a possibility for numerical calculation of the resulting phase thickness during the co-extrusion of aluminium and steel, by means of Lateral Angular Co-Extrusion (LACE), is presented. In the first step, an analogy test on a forming dilatometer was developed for the experimental investigation of the intermetallic phase formation. The width of the intermetallic phase seam was determined by means of scanning electron microscopy using an image processing tool. Based on the experimental results, a calculation instruction was defined to describe the intermetallic phase thickness as a function of temperature and contact time. The function was implemented in a commercial finite element (FE) software by means of a user-defined subroutine and validated on the basis of experimental data.

引用

页数：6

共 15 条

[11]

Rummel G., 1995, Z METALLKUNDE, V95a

[12] On the formation and growth of intermetallic phases during interdiffusion between low-carbon steel and aluminum alloys [J].

Springer, H. ;

Kostka, A. ;

Payton, E. J. ;

Raabe, D. ;

Kaysser-Pyzalla, A. ;

Eggeler, G. .

ACTA MATERIALIA, 2011, 59 (04) :1586-1600

[13] Co-Extrusion of Semi-Finished Aluminium-Steel Compounds [J].

Thuerer, S. E. ;

Uhe, J. ;

Golovko, O. ;

Bonk, C. ;

Bouguecha, A. ;

Klose, C. ;

Behrens, B. -A. ;

Maier, H. J. .

PROCEEDINGS OF THE 20TH INTERNATIONAL ESAFORM CONFERENCE ON MATERIAL FORMING (ESAFORM 2017), 2017, 1896

[14]

Thurer Susanne Elisabeth, 2017, Key Engineering Materials, V742, P512, DOI 10.4028/www.scientific.net/KEM.742.512

[15] Formation of intermetallic compounds in friction bonding of Al alloys to steel [J].

Yamamoto, Naotsugu ;

Takahashi, Makoto ;

Aritoshi, Masatoshi ;

Ikeuchi, Kenji .

THERMEC 2006, PTS 1-5, 2007, 539-543 :3865-+

← 1 2 →