Effects of residual stress on fracture toughness and subcritical growth of indented cracks in glasses

被引：0
|
作者：
Yoda, M
Ogawa, N
Ikeda, N
Kubota, A
机构：
来源：
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III | 1996年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fracture and subcritical crack growth were investigated using indented cracks in soda-lime glass, aluminosilicate glass and; borosilicate glass. The effect of residual stress was experimentally determined by obtaining the fracture toughnesses for cracks of various lengths. Extended cracks of various lengths-were produced at the same indentation load. From the results, dimensionless indenter-material constants chi(r) were determined for the surface crack and depth crack of semi-elliptical shape. Subcritical crack growth data for the as-indented short cracks show anomalous behavior, i.e. negative dependence of crack velocity on the stress intensity factor during small crack growth. This decrease in the crack velocity for the as-indented short crack can be explained by taking account of the residual stress.
引用
收藏
页码：727 / 732
页数：6
相关论文
共 50 条
  • [21] Effect of surface residual stress on the fracture of double cantilever beam fracture toughness specimen
    Wang, B. L.
    Wang, K. F.
    JOURNAL OF APPLIED PHYSICS, 2013, 113 (15)
  • [22] Residual stress effects on cleavage fracture
    Sherry, A. H.
    Lee, K. S.
    Goldthorpe, M. R.
    Beardsmore, D. W.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE 2007, VOL 6: MATERIALS AND FABRICATION, 2007, : 537 - 543
  • [23] Effect of residual stress due to sintering on fracture toughness of cemented carbides
    Yohe, W.C.
    Metal Powder Report, 2001, 56 (03)
  • [24] Effect of Residual Stress on Fracture Parameters of through Cracks in Welded Plates
    Seifi, Rahman
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10 : 1895 - 1900
  • [25] Study on the effect of compressive residual stress on fracture toughness of spring steel
    Huh, SC
    Park, WJ
    Park, SH
    Lee, SH
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 2423 - 2428
  • [26] Mixed mode fracture toughness of adhesively bonded joints with residual stress
    Shimamoto, Kazumasa
    Sekiguchi, Yu
    Sato, Chiaki
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2016, 102 : 120 - 126
  • [27] Fracture toughness and residual stress measurements in tempered glass by Hertzian indentation
    Petit, F.
    Sartieaux, A. C.
    Gonon, M.
    Cambier, F.
    ACTA MATERIALIA, 2007, 55 (08) : 2765 - 2774
  • [28] Effect of vibratory weld conditioning on valve residual stress and fracture toughness
    Lu, Qinghua
    Chen, Ligong
    Ni, Chunzhen
    PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON MECHANICAL ENGINEERING AND MECHANICS 2007, VOLS 1 AND 2, 2007, : 1044 - 1048
  • [29] THE EFFECTS OF CRACK GROWTH HISTORY ON FRACTURE TOUGHNESS
    Probert, M. A.
    Coules, H. E.
    Truman, C. E.
    Hofmann, M.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, 2019, VOL 6A, 2019,
  • [30] Fracture toughness and subcritical crack growth of small crack in silicon nitride at room temperature
    Ogasawara, T.
    Hirosaki, N.
    Akimune, Y.
    Yasuda, E.
    Yogyo Kyokai Shi/Journal of the Ceramic Society of Japan, 1995, 103 (10): : 1063 - 1068
12345