Effects of residual stress on fracture toughness and subcritical growth of indented cracks in glasses

被引：0
|
作者：
Yoda, M
Ogawa, N
Ikeda, N
Kubota, A
机构：
来源：
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III | 1996年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fracture and subcritical crack growth were investigated using indented cracks in soda-lime glass, aluminosilicate glass and; borosilicate glass. The effect of residual stress was experimentally determined by obtaining the fracture toughnesses for cracks of various lengths. Extended cracks of various lengths-were produced at the same indentation load. From the results, dimensionless indenter-material constants chi(r) were determined for the surface crack and depth crack of semi-elliptical shape. Subcritical crack growth data for the as-indented short cracks show anomalous behavior, i.e. negative dependence of crack velocity on the stress intensity factor during small crack growth. This decrease in the crack velocity for the as-indented short crack can be explained by taking account of the residual stress.
引用
收藏
页码：727 / 732
页数：6
相关论文
共 50 条
  • [11] Nickel-alumina interfacial fracture toughness: Experiments and analysis of residual stress effects
    Thurston, ME
    Zehnder, AT
    INTERNATIONAL JOURNAL OF FRACTURE, 1996, 76 (03) : 221 - 241
  • [12] The effects of residual stress, loading, and crack geometry on SERE fracture toughness test results
    Grendahl, S
    Bert, R
    Cho, K
    Bar-On, I
    JOURNAL OF TESTING AND EVALUATION, 2001, 29 (03) : 271 - 276
  • [13] Evolution of fracture mechanics parameters for cracks in residual stress fields
    Matvienko, Yu.
    Eleonsky, S.
    Pisarev, V.
    IGF WORKSHOP FRACTURE AND STRUCTURAL INTEGRITY, 2018, 9 : 16 - 21
  • [14] RESIDUAL STRESS AND FRACTURE TOUGHNESS OF PIRAC TITANIUM NITRIDE COATINGS
    Wu, Siyuan
    Zhang, Guoyun
    Wu, Shoujun
    Su, Yu
    SURFACE REVIEW AND LETTERS, 2017, 24 (04)
  • [15] Effect of residual stress on interlaminar fracture toughness of CFRP laminates
    Arai, Masahiro
    Sumida, Takeshi
    Shimizu, Masayoshi
    JOURNAL OF THERMAL STRESSES, 2007, 30 (11) : 1099 - 1116
  • [16] Measurement and modelling of residual stress effects on cracks
    Sherry, A. H.
    da Fonseca, J. Quinta
    Goldthorpe, M. R.
    Taylor, K.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2007, 30 (03) : 243 - 257
  • [17] Testing study of subcritical crack growth rate and fracture toughness in different rocks
    曹平
    李江腾
    袁海平
    TransactionsofNonferrousMetalsSocietyofChina, 2006, (03) : 709 - 713
  • [18] Testing study of subcritical crack growth rate and fracture toughness in different rocks
    Cao Ping
    Li Jiang-teng
    Yuan Hai-ping
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 (03) : 709 - 713
  • [19] Influence of relative humidity on fracture toughness of rock: Implications for subcritical crack growth
    Nara, Yoshitaka
    Morimoto, Kazuya
    Hiroyoshi, Naoki
    Yoneda, Tetsuro
    Kaneko, Katsuhiko
    Benson, Philip M.
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2012, 49 (18) : 2471 - 2481
  • [20] Intrinsic and extrinsic effects on the fracture toughness of ductile metallic glasses
    Li, Hong
    Pei, Qing-Xiang
    Sha, Zhen-Dong
    Branicio, Paulo S.
    MECHANICS OF MATERIALS, 2021, 162
12345