Effects of residual stress on fracture toughness and subcritical growth of indented cracks in glasses

被引：0
|
作者：
Yoda, M
Ogawa, N
Ikeda, N
Kubota, A
机构：
来源：
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III | 1996年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fracture and subcritical crack growth were investigated using indented cracks in soda-lime glass, aluminosilicate glass and; borosilicate glass. The effect of residual stress was experimentally determined by obtaining the fracture toughnesses for cracks of various lengths. Extended cracks of various lengths-were produced at the same indentation load. From the results, dimensionless indenter-material constants chi(r) were determined for the surface crack and depth crack of semi-elliptical shape. Subcritical crack growth data for the as-indented short cracks show anomalous behavior, i.e. negative dependence of crack velocity on the stress intensity factor during small crack growth. This decrease in the crack velocity for the as-indented short crack can be explained by taking account of the residual stress.
引用
收藏
页码：727 / 732
页数：6
相关论文
共 50 条
  • [1] FRACTURE AND SUBCRITICAL GROWTH-CHARACTERISTICS OF INDENTED CRACKS IN SODA-LIME GLASS
    YODA, M
    NAGAO, M
    ENGINEERING FRACTURE MECHANICS, 1993, 46 (05) : 789 - 796
  • [2] Fracture toughness and subcritical crack growth in polycrystalline silicon
    Chasiotis, I.
    Cho, S. W.
    Jonnalagadda, K.
    JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 2006, 73 (05): : 714 - 722
  • [3] Effects of High Toughness and Welding Residual Stress for Unstable Fracture Prevention
    An, Gyubaek
    Park, Jeongung
    Han, Ilwook
    APPLIED SCIENCES-BASEL, 2020, 10 (23): : 1 - 12
  • [4] Welding Residual Stress Effect in Fracture Toughness
    An, Gyubaek
    Woo, Wanchuck
    Park, Jeongung
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2019, 19 (04) : 2323 - 2328
  • [5] Processing effects on fracture toughness of metallic glasses
    Chen, Wen
    Zhou, Haofei
    Liu, Ze
    Ketkaew, Jittisa
    Li, Ning
    Yurko, James
    Hutchinson, Nicholas
    Gao, Huajian
    Schroers, Jan
    SCRIPTA MATERIALIA, 2017, 130 : 152 - 156
  • [6] CHEMICAL STRESS APPLIED TO CREEP AND FRACTURE THEORIES .2. APPLICATION TO GROWTH OF SUBCRITICAL GRIFFITH CRACKS
    PULS, MP
    DUTTON, R
    STEVENS, RN
    ACTA METALLURGICA, 1974, 22 (05): : 639 - 647
  • [7] Evaluation of residual stress corrections to fracture toughness values
    Hill, Michael R.
    Vandalen, John E.
    Journal of ASTM International, 2008, 5 (08):
  • [8] Influence of residual stress in measurement of apparent fracture toughness
    Lewis, S. J.
    Smith, D. J.
    Booker, J. D.
    Truman, C. E.
    ENGINEERING STRUCTURAL INTEGRITY: RESEARCH, DEVELOPMENT AND APPLICATION, VOLS 1 AND 2, 2007, : 448 - 451
  • [9] Influence of subcritical crack growth on the determination of fracture toughness in brittle materials
    Krautgasser, C.
    Chlup, Z.
    Supancic, P.
    Danzer, R.
    Berrnejo, R.
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2016, 36 (05) : 1307 - 1312
  • [10] Testing study of subcritical crack growth velocity and fracture toughness of marble
    李江腾
    曹平
    袁海平
    Journal of Coal Science & Engineering(China), 2005, (01) : 23 - 25
12345