Ternary Zr-Nb-Fe(O) system:: phase diagram at 853 K and corrosion behaviour in the domain Nb <0.8%

被引:50
作者
Barberis, P
Charquet, D
Rebeyrolle, V
机构
[1] CEZUS Res Ctr, F-73403 Ugine, France
[2] ANP, FRAMATOME, F-69456 Lyon 06, France
关键词
D O I
10.1016/j.jnucmat.2004.01.007
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Several zirconium-based alloys in the domain Nb < 0.8 wt%, Fe < 0.5 wt% and Sn < 1 wt% (and oxygen in the range 600-1200 ppm) were elaborated. Several process routes were used to produce sheets and claddings. The microstructure was investigated by TEM, with a particular attention payed to the SPP nature and composition. Corrosion tests in steam in autoclave or in air were performed. This study allowed us to precise the isothermal cut at 853 K of the Zr-rich corner of the Zr-Nb-Fe ternary phase diagram, and particularly the solubility limit of Nb in alphaZr which appears equal to 0.37+/-0.05 wt%, which is much lower than the usually assumed value of 0.6 wt%. In the investigated range, the tin content has no significant influence on the phase diagram, but tin degrades the corrosion resistance in autoclave at 773 and 688 K. Last, the steam corrosion behaviour shows a very strong dependence on the exact process for the lowest SPP-VF, and very high weight gain can be obtained. The air oxidation is much less affected by this parameter. (C) 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码:163 / 174
页数:12
相关论文
共 30 条
[1]   Role of the second-phase particles in zirconium binary alloys [J].
Barberis, P ;
Ahlberg, E ;
Simic, N ;
Charquet, D ;
Lemaignan, C ;
Wikmark, G ;
Dahlbäck, M ;
Limbäck, M ;
Tägtström, P ;
Lehtinen, B .
ZIRCONIUM IN THE NUCLEAR INDUSTRY: THIRTEENTH INTERNATIONAL SYMPOSIUM, 2002, 1423 :33-55
[2]   STUDY OF THE SOLUBILITY OF IRON IN ZIRCONIUM BY THERMOELECTRIC-POWER MEASUREMENTS [J].
BORRELLY, R ;
MERLE, P ;
ADAMI, L .
JOURNAL OF NUCLEAR MATERIALS, 1990, 170 (02) :147-156
[3]   Corrosion of zirconium alloys: Link between the metal/oxide interface roughness, the degradation of the protective oxide layer and the corrosion kinetics [J].
Bossis, P ;
Lefebvre, F ;
Barberis, P ;
Galerie, A .
HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 :255-262
[4]  
Bossis P., 1999, THESIS
[5]   Phase transition temperature in the Zr-rich corner of Zr-Nb-Sn-Fe alloys [J].
Canay, M ;
Danón, CA ;
Arias, D .
JOURNAL OF NUCLEAR MATERIALS, 2000, 280 (03) :365-371
[6]   EFFECT OF COMPOSITION AND HEAT-TREATMENT ON THE MICROSTRUCTURE AND CORROSION BEHAVIOR OF ZR-NB ALLOYS [J].
CHOO, KN ;
KANG, YH ;
PYUN, SI ;
URBANIC, VF .
JOURNAL OF NUCLEAR MATERIALS, 1994, 209 (03) :226-235
[7]   The interaction of plasticity and diffusion controlled precipitation reactions [J].
Embury, JD ;
Deschamps, A ;
Brechet, Y .
SCRIPTA MATERIALIA, 2003, 49 (10) :927-932
[8]   In-PWR irradiation performance of dilute tin-zirconium advanced alloys [J].
Garde, AA ;
Smith, GP ;
Pirek, RC .
ZIRCONIUM IN THE NUCLEAR INDUSTRY: THIRTEENTH INTERNATIONAL SYMPOSIUM, 2002, 1423 :490-504
[9]   Experimental investigation of the Zr corner of the ternary Zr-Nb-Fe phase diagram [J].
Granovsky, MS ;
Canay, M ;
Lena, E ;
Arias, D .
JOURNAL OF NUCLEAR MATERIALS, 2002, 302 (01) :1-8
[10]   Effect of β phase, precipitate and Nb-concentration in matrix on corrosion and oxide characteristics of Zr-xNb alloys [J].
Jeong, YH ;
Kim, HG ;
Kim, TH .
JOURNAL OF NUCLEAR MATERIALS, 2003, 317 (01) :1-12