Compatibility of Lead-Bismuth Eutectic with SiC-Coated Graphite at Elevated Temperature

被引：10

作者：

Chakraborty, Poulami ^{[1
]}

Ghosh, Abhijit ^{[2
]}

Dey, Gautam Kumar ^{[3
]}

机构：

[1] Bhabha Atom Res Ctr, Fus Reactor Mat Sect, Bombay 400085, Maharashtra, India

[2] Bhabha Atom Res Ctr, Glass & Adv Mat Div, Bombay 400085, Maharashtra, India

[3] Bhabha Atom Res Ctr, Div Mat Sci, Bombay 400085, Maharashtra, India

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE | 2017年 / 48卷 / 01期

关键词：

REACTOR SYSTEMS; CORROSION; ALLOY;

D O I：

10.1007/s11663-016-0763-1

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Uniform coating of beta-silicon carbide (beta-SiC) was formed over a graphite pellet through slurry-based silicon coating followed by in situ reaction at 1873 K (1600 A degrees C). The coated pellet was exposed to molten lead-bismuth eutectic (LBE) at 1173 K (900 A degrees C) in static condition for 200 h. Weight loss measurement, X-ray diffraction, and secondary electron microscopy-energy-dispersive spectroscopy confirmed that the SiC coating could effectively prevent molten LBE from attacking the inner graphite material.

引用

页码：1 / 5

页数：5

共 15 条

[1] Allen T., 2007, Science and Technology of Nuclear Installations, V2007, P1, DOI [https://doi.org/10.1155/2007/97486, DOI 10.1155/2007/97486]
[2] [Anonymous], 2015, LBE HDB
[3] An overview of corrosion issues for the design and operation of high-temperature lead- and lead-bismuth-cooled reactor systems
Ballinger, RG
Lim, J
[J]. NUCLEAR TECHNOLOGY, 2004, 147 (03) : 418 - 435
[4] High temperature reactors
Dulera, I. V.
Sinha, R. K.
[J]. JOURNAL OF NUCLEAR MATERIALS, 2008, 383 (1-2) : 183 - 188
[5] Hillinger G.N., 1986, NATURE, V54, P357
[6] Corrosion behaviour of martensitic and austenitic steels in flowing lead-bismuth eutectic
Martin-Munoz, F. J.
Soler-Crespo, L.
Gomez-Briceno, D.
[J]. JOURNAL OF NUCLEAR MATERIALS, 2011, 416 (1-2) : 87 - 93
[7] CORROSION CHARACTERISTICS OF SILICON-CARBIDE AND SILICON-NITRIDE
MUNRO, RG
DAPKUNAS, SJ
[J]. JOURNAL OF RESEARCH OF THE NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY, 1993, 98 (05) : 607 - 631
[8] Olesinki R.W., 1984, Bull. Alloy Phase Diagrams, V5, P271, DOI DOI 10.1007/BF02868551
[9] Olesinski R.W., 1985, B ALLOY PHASE DIAGR, V6, P359, DOI DOI 10.1007/BF02880522
[10] Sengupta AK, 2006, INT J MATER RES, V97, P834

← 1 2 →