Al-9.00 %Si-0.25 %Mg alloys modified by ytterbium

被引：18

作者：

Jia, Kun ^{[1
]}

Yu, Wen-Bin ^{[1
]}

Yao, Jian-Min ^{[1
]}

Zhang, Shuo ^{[1
]}

Wu, Hao ^{[2
]}

机构：

[1] Southwest Univ, Sch Mat Sci & Engn, Chongqing 400715, Peoples R China

[2] Guangzhou Automobile Grp Motor Co Ltd, Guangzhou 510030, Guangdong, Peoples R China

来源：

RARE METALS | 2017年 / 36卷 / 02期

关键词：

Al-9.00 %Si-0.25 %Mg alloy; Yb; Modification; Eutectic silicon; MECHANICAL-PROPERTIES; EUTECTIC MODIFICATION;

D O I：

10.1007/s12598-014-0378-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of ytterbium (Yb) on microstructure and solidification behavior of Al-9.00 %Si-0.25 %Mg alloys were investigated. By optical microscope (OM) and scanning electron microscopy (SEM), it is found that the morphology of eutectic silicon changes from coarse plates to fine fibers by the addition of 0.7 %wt Yb. In addition, the grains of alpha-Al matrix are refined by Yb addition. Phase constitution of the alloy was analyzed by X-ray diffractometer (XRD) and energy dispersive spectroscopy (EDS) attached with SEM and mechanical properties were measured by hardness test. It is concluded that the Yb atoms are incorporated into the silicon by the adsorption at the solid-liquid growth front to cause the modification of eutectic silicon. Furthermore, the results of XRD and EDS analysis reveal that the Yb-containing phase forming in the alloys is Al3Yb.

引用

页码：95 / 100

页数：6

共 24 条

[1]

Binnewies M., 2002, THERMOCHEMICAL DATA, P783

[2]

Dahle AK, 2001, MAT SCI ENG A-STRUCT, V32, P243

[3]

Knuutinen A., 2001, Journal of Light Metals, V1, P241, DOI [10.1016/S1471-5317(02)00006-8, DOI 10.1016/S1471-5317(02)00006-8]

[4]

Knuutinen A., 2001, Journal Light Metals, V1, P229, DOI [10.1016/S1471-5317(02)00004-4, DOI 10.1016/S1471-5317(02)00004-4]

[5]

Kranenberg C, 1999, Z ANORG ALLG CHEM, V625, P1787, DOI 10.1002/(SICI)1521-3749(199911)625:11<1787::AID-ZAAC1787>3.0.CO

[6]

2-H

[7] The effect of grain refinement and silicon content on grain formation in hypoeutectic Al-Si alloys [J].

Lee, YC ;

Dahle, AK ;

StJohn, DH ;

Hutt, JEC .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 259 (01) :43-52

[8] Microstructure evolution and modification mechanism of the ytterbium modified Al-7.5%Si-0.45%Mg alloys [J].

Li, Bao ;

Wang, Hongwei ;

Jie, Jinchuan ;

Wei, Zunjie .

JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (07) :3387-3392

[9]

Li HL, 2006, BEHAV ANTIMONY AI SI, P27

[10] THE MECHANISM OF SILICON MODIFICATION IN ALUMINUM-SILICON ALLOYS - IMPURITY INDUCED TWINNING [J].

LU, SZ ;

HELLAWELL, A .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (10) :1721-1733

← 1 2 3 →