Enhanced tribology durability of a self-assembled monolayer of alkylphosphonic acid on a textured copper substrate

被引：28
作者：
Wan, Yong [1 ]
Wang, Yinhu [1 ]
Zhang, Quan [1 ]
Wang, Zhongqian [1 ]
Xu, Zhen [1 ]
Liu, Changsong [1 ]
Zhang, Junyan [2 ]
机构：
[1] Qingdao Technol Univ, Sch Mech Engn, Qingdao 266033, Peoples R China
[2] Chinese Acad Sci, State Key Lab Solid Lubricat, Lanzhou Inst Chem Phys, Lanzhou 730000, Peoples R China
来源：
APPLIED SURFACE SCIENCE | 2012年 / 259卷
关键词：
Thin film; Friction; Self-assembled monolayer; Chemical etching; Copper; NATIVE-OXIDE SURFACE; MAGNESIUM ALLOY AZ31; ALKANEPHOSPHONIC ACIDS; FRICTION; ALUMINUM; ADHESION; SPECTROSCOPY; CHEMISTRY; MECHANISM; TITANIUM;
D O I：
10.1016/j.apsusc.2012.07.008
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
A simple two-step process was developed to render the copper surface with lower friction and long durability. The copper substrate was immersed in a 0.01 M NaOH solution to fabricate a textured Cu2O film. A self-assembled monolayer of alkylphosphonic acid was then deposited on the Cu2O film to acquire high hydrophobicity. Scanning electron microscopy, Fourier transform infrared microscopy and water contact angle measurements were used to analyze the morphological features, the chemical composition and hydrophobicity of freshly prepared samples, respectively. Moreover, the friction-reducing behavior of the organic-inorganic composite film sliding against steel was evaluated in a ball-on-plate configuration. It was found that the alkylphosphonic acid films on the textured Cu2O film led to decreased friction with significantly extended life. For a constant load, the increase in chain length of alkylphosphonic acid yields the films that are dramatically more stable against tribological deformation and provide low coefficients of friction over much longer periods of time. (C) 2012 Elsevier B. V. All rights reserved.
引用
收藏
页码：147 / 152
页数：6
相关论文
共 49 条
[1]   Self assembled monolayers on silicon for molecular electronics [J].
Aswal, D. K. ;
Lenfant, S. ;
Guerin, D. ;
Yakhmi, J. V. ;
Vuillaume, D. .
ANALYTICA CHIMICA ACTA, 2006, 568 (1-2) :84-108
[2]   Underpotentially deposited copper promotes self-assembly of alkanephosphonate monolayers on gold substrates [J].
Baker, MV ;
Jennings, GK ;
Laibinis, PE .
LANGMUIR, 2000, 16 (07) :3288-3293
[3]   Scale effects in dry and wet friction, wear, and interface temperature [J].
Bhushan, B ;
Nosonovsky, M .
NANOTECHNOLOGY, 2004, 15 (07) :749-761
[4]   Tribological Durability of Silane Monolayers on Silicon [J].
Booth, Brandon D. ;
Vilt, Steven G. ;
Ben Lewis, J. ;
Rivera, Jose L. ;
Buehler, Edward A. ;
McCabe, Clare ;
Jennings, G. Kane .
LANGMUIR, 2011, 27 (10) :5909-5917
[5]   Wettability of porous surfaces. [J].
Cassie, ABD ;
Baxter, S .
TRANSACTIONS OF THE FARADAY SOCIETY, 1944, 40 :0546-0550
[6]   Self-assembled monolayer of alkanephosphoric acid on nanotextured Ti [J].
Clair, Sylvain ;
Variola, Fabio ;
Kondratenko, Mykola ;
Jedrzejowski, Pawel ;
Nanci, Antonio ;
Rosei, Federico ;
Perepichka, Dmitrii F. .
JOURNAL OF CHEMICAL PHYSICS, 2008, 128 (14)
[7]   Mechanism of copper removal during CMP in acidic H2O2 slurry [J].
Du, T ;
Tamboli, D ;
Desai, V ;
Seal, S .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2004, 151 (04) :G230-G235
[8]   Anchoring of sulfur-containing alkylphosphonic and semifluorinated alkylphosphonic molecules on a polycrystalline aluminum substrate [J].
Fonder, G. ;
Delhalle, J. ;
Essahli, M. ;
Ameduri, B. ;
Mekhalif, Z. .
SURFACE AND INTERFACE ANALYSIS, 2008, 40 (02) :85-96
[9]   Anchoring of alkylphosphonic derivatives molecules on copper oxide surfaces [J].
Fonder, Gregory ;
Minet, Isabelle ;
Volcke, Cedric ;
Devillers, Sebastien ;
Delhalle, Joseph ;
Mekhalif, Zineb .
APPLIED SURFACE SCIENCE, 2011, 257 (14) :6300-6307
[10]   Enhanced bonding of alkanephosphonic acids to oxidized titanium using surface-bound alkoxyzirconium complex interfaces [J].
Gawalt, ES ;
Lu, G ;
Bernasek, SL ;
Schwartz, J .
LANGMUIR, 1999, 15 (26) :8929-8933
12345