Synthesis of monophase Al4O4C and the effect of Al4O4C addition to MgO-C refractory

被引：51

作者：

Yu, Chao ^{[1
]}

Zhu, Hongxi ^{[1
]}

Yuan, Wenjie ^{[1
]}

Deng, Chengji ^{[1
]}

Cui, Peng ^{[1
]}

Zhou, Shimin ^{[1
]}

机构：

[1] Wuhan Univ Sci & Technol, State Key Lab Breeding Base Refractories & Ceram, Wuhan 430081, Peoples R China

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2013年 / 579卷

基金：

中国国家自然科学基金;

关键词：

Al4O4C; Synthesis; Aluminum content; Antioxidant; Oxidation; HEAT-TREATMENT; ALUMINUM; TEMPERATURE; POWDER; BRICKS; SIZE; AL;

D O I：

10.1016/j.jallcom.2013.06.088

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Monophase Al4O4C ceramic powder was synthesized using a mixture of alpha-alumina, carbon black and aluminum powders as raw materials. The effects of different starting compositions and raw materials ratio on the phase transformation and micromorphology of Al4O4C were investigated. The results indicated that alpha-alumina, carbon black and aluminum powders was more appropriate as raw materials, and 20 mol% excess of aluminum resulted in single phase Al4O4C. Al2OC would occur if excessive carbon black was used. The Al content was found to have a significant effect on the microstructure of synthesized Al4O4C. Al4O4C added to the MgO-C refractory initially reacts with CO to form Al2O3 and C. After the reaction, the formed Al2O3 will further react with MgO to form MgAl2O4. The above reaction processes can form protective layers on the surfaces of the refractories, which inhibit the oxidation of the refractories. (c) 2013 Elsevier B.V. All rights reserved.

引用

页码：348 / 354

页数：7

共 50 条

[31] In-situ catalytic growth of MgAl2O4 spinel whiskers in MgO-C refractories
Zhu, Boquan
Wei, Guoping
Li, Xiangcheng
Ma, Zheng
Wei, Ying
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2014, 105 (06) : 593 - 598
[32] Thermodynamic evaluation of SiC oxidation in Al2O3-MgAl2O4-SiC-C refractory castables
Luz, A. P.
Pandolfelli, V. C.
CERAMICS INTERNATIONAL, 2010, 36 (06) : 1863 - 1869
[33] Synthesis and Characterization of [M2(OH)2(C4O4)2(H2O)4]•2H2O (M = Al or Ga)
Halis, Selda
Reinsch, Helge
Stock, Norbert
ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 2016, 642 (23): : 1340 - 1344
[34] Surface chemistry modification for elimination of hydrophilic Al4C3 in B4C/Al composites
Trujillo-Vazquez, E.
Pech-Canul, M. I.
Guia-Tello, J. C.
Pech-Canul, M. A.
MATERIALS & DESIGN, 2016, 89 : 94 - 101
[35] Preparation of B4C-Al and B4C-Al-CNT Composite Materials by Means of Infiltration
Karagedov, G. R.
CHEMISTRY FOR SUSTAINABLE DEVELOPMENT, 2024, 32 (04): : 415 - 421
[36] Comparison of nanostructured Al/B4C composite produced by ARB and Al/B4C composite produced by RRB process
Alizadeh, Morteza
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 528 (02): : 578 - 582
[37] The influence of B4C and MgB2 additions on the behavior of MgO-C bricks
Campos, Karma S.
Lenz e Silva, Guilherme F. B.
Nunes, Eduardo H. M.
Vasconcelos, Wander L.
CERAMICS INTERNATIONAL, 2012, 38 (07) : 5661 - 5667
[38] Effect of B4C Granulometric Composition on Microstructure and Mechanical Properties of B4C-Al Composites
Lu Peng
Ru Hongqiang
Yue Xinyan
Yu Liang
Sun Xudong
RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 536 - 540
[39] Reaction Process of Al8B4C7 Synthesized from Al2O3/B2O3/C Mixed Powder
Cui Peng
Yuan Wenjie
Deng Chengji
Zhu Hongxi
Fan Mingyu
Huang Yongliang
RARE METAL MATERIALS AND ENGINEERING, 2013, 42 : 898 - 900
[40] Formation of MgAl2O4 at Al/MgO Interface
Yang, Lin
Xia, Mingxu
Babu, Nadendla Hari
Li, Jianguo
MATERIALS TRANSACTIONS, 2015, 56 (03) : 277 - 280

← 1 2 3 4 5 →