Activated reaction synthesis of silicon oxynitride from silica and silicon nitride

被引:6
作者
Fruhstorfer, Jens [1 ]
Kerber, Florian [1 ]
Weigelt, Christian [1 ]
Moritz, Kirsten [1 ]
Aneziris, Christos G. [1 ]
机构
[1] TU Bergakad Freiberg, Inst Ceram Glass & Construct Mat, Agricolastr 17, D-09596 Freiberg, Germany
关键词
Dispersant amount; Activated sintering; Si2N2O; Sinoite; Refractory additive; MECHANICAL-PROPERTIES; SI2N2O; OXIDATION; BEHAVIOR; ALUMINA; POWDERS; SLIPS;
D O I
10.1016/j.ceramint.2018.02.044
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
This study investigates the preparation of samples with equimolar parts of silica and silicon nitride and the subsequent reaction synthesis of silicon oxynitride. The influence of the raw material and the processing parameters on the conversion yield was analyzed. In detail, the effects of the silica crystallinity and of the grain size of the silicon nitride were investigated. Furthermore, the reaction synthesis was activated by magnesium hydroxide or calcium hydroxide. The samples were prepared by slip casting in plaster molds. Firstly, the optimal dispersant type, a synthetic polyelectrolyte, was determined. For the batches with the finer silicon nitride the measured optimal amount was 0.6 wt%. For the batches with the coarser silicon nitride it was 0.18 wt%. From the cast and demolded samples, broken pieces were fired at 1550 degrees C for 1, 8 or 15 h in nitrogen atmosphere. The conversion yield of silicon oxynitride was analyzed by quantitative X-ray diffraction. The fraction of silicon oxynitride increased with extended holding time at the sintering temperature, by the use of fine silicon nitride, and by the addition of magnesium hydroxide as sintering additive. The silica crystallinity had no statistically significant effect. The obtained maximum conversion yield was 92 wt%.
引用
收藏
页码:8467 / 8475
页数:9
相关论文
共 41 条
[1]  
Albano MP, 1998, J AM CERAM SOC, V81, P837, DOI 10.1111/j.1151-2916.1998.tb02417.x
[2]  
[Anonymous], R LANG ENV STAT COMP
[3]  
[Anonymous], 2006, RHEOLOGY HDB
[4]  
Anthony J.W., 2007, Handbook of Mineralogy
[5]   SI3N4 AND SI2N2O FOR HIGH-PERFORMANCE RADOMES [J].
BARTA, J ;
MANELA, M ;
FISCHER, R .
MATERIALS SCIENCE AND ENGINEERING, 1985, 71 (1-2) :265-272
[6]  
Benesty J, 2009, SPRINGER TOP SIGN PR, V2, P37, DOI 10.1007/978-3-642-00296-0_5
[7]   Influence of different oxides on the formation of Si2N2O from SiO2 and Si3N4 [J].
Bergman, Bill ;
Huang, Heping .
Journal of the European Ceramic Society, 1990, 6 (01) :3-8
[8]  
Billy M., 1981, Ceramics International, V7, P13, DOI 10.1016/0272-8842(81)90033-X
[9]   Aqueous tape casting of silicon nitride [J].
Bitterlich, B ;
Heinrich, JG .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (13) :2427-2434
[10]   Carbon-Bonded Alumina Refractories with Reduced Carbon Content due to the Addition of Semi-Conductive Silicon and/or Nanoparticles [J].
Brachhold, N. ;
Fruhstorfer, J. ;
Mertke, A. ;
Aneziris, C. G. .
JOURNAL OF CERAMIC SCIENCE AND TECHNOLOGY, 2016, 7 (02) :209-221