Pyrolysis of apple pulp:: chemical activation with phosphoric acid

被引：125
作者：
Suárez-García, F [1 ]
Martínez-Alonso, A [1 ]
Tascón, JMD [1 ]
机构：
[1] CSIC, Inst Nacl Carbon, Oviedo 33080, Spain
来源：
JOURNAL OF ANALYTICAL AND APPLIED PYROLYSIS | 2002年 / 63卷 / 02期
关键词：
apple pulp; biomass; pyrolysis; activated carbon; adsorption; surface area; porosity;
D O I：
10.1016/S0165-2370(01)00160-7
中图分类号：
O65 [分析化学];
学科分类号：
070302 ; 081704 ;
摘要：
Chemical activation of apple pulp with phosphoric acid has been carried out to prepare activated carbons. The materials were characterized by elemental analysis, N-2 adsorption (77 K), CO2 adsorption (273 K) and X-ray diffraction. The effects of temperature, soaking time, impregnation ratio and degree of washing were studied. Maximum development of porosity was observed upon beating to 723 K plus 1 h soaking. The amount of phosphoric acid used in the impregnation step strongly influenced the porous texture, micropores being predominant at low impregnation ratios whereas larger amounts of phosphoric acid produced wide micropores and mesopores. The washing sep also had a crucial effect on the porosity accessible to different adsorbates. The results suggest the feasibility of the process from the point of view of both porous texture and carbon yield. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：283 / 301
页数：19
相关论文
共 28 条
  • [1] The preparation of activated carbon from macadamia nutshell by chemical activation
    Ahmadpour, A
    Do, DD
    [J]. CARBON, 1997, 35 (12) : 1723 - 1732
  • [2] Influence of the atmosphere in the chemical activation of wood by phosphoric acid
    Benaddi, H
    Legras, D
    Rouzaud, JN
    Beguin, F
    [J]. CARBON, 1998, 36 (03) : 306 - 309
  • [3] Comparative performance of X-ray diffraction and Raman microprobe techniques for the study of carbon materials
    Cuesta, A
    Dhamelincourt, P
    Laureyns, J
    Martínez-Alonso, A
    Tascón, JMD
    [J]. JOURNAL OF MATERIALS CHEMISTRY, 1998, 8 (12) : 2875 - 2879
  • [4] USE OF N2 VS CO2 IN THE CHARACTERIZATION OF ACTIVATED CARBONS
    GARRIDO, J
    LINARESSOLANO, A
    MARTINMARTINEZ, JM
    MOLINASABIO, M
    RODRIGUEZREINOSO, F
    TORREGROSA, R
    [J]. LANGMUIR, 1987, 3 (01) : 76 - 81
  • [5] Activated carbon from cotton stalks by impregnation with phosphoric acid
    Girgis, BS
    Ishak, MF
    [J]. MATERIALS LETTERS, 1999, 39 (02) : 107 - 114
  • [6] ACTIVATED CARBON FROM SUGAR-CANE BAGASSE BY CARBONIZATION IN THE PRESENCE OF INORGANIC ACIDS
    GIRGIS, BS
    KHALIL, LB
    TAWFIK, TAM
    [J]. JOURNAL OF CHEMICAL TECHNOLOGY AND BIOTECHNOLOGY, 1994, 61 (01) : 87 - 92
  • [7] KIRK RE, 1962, ENCICLOPEDIA TECNOLO, V10, P301
  • [8] FACTORS AFFECTING THE PREPARATION OF ACTIVATED CARBONS FROM COCONUT SHELL CATALYZED BY POTASSIUM
    LAINE, J
    CALAFAT, A
    [J]. CARBON, 1991, 29 (07) : 949 - 953
  • [9] PREPARATION AND CHARACTERIZATION OF ACTIVATED CARBONS FROM COCONUT SHELL IMPREGNATED WITH PHOSPHORIC-ACID
    LAINE, J
    CALAFAT, A
    LABADY, M
    [J]. CARBON, 1989, 27 (02) : 191 - 195
  • [10] Microporous texture of activated carbon fibers prepared from aramid fiber pulp
    MartinezAlonso, A
    Jamond, M
    MontesMoran, MA
    Tascon, JMD
    [J]. MICROPOROUS MATERIALS, 1997, 11 (5-6): : 303 - 311
123