Effects of Heat Treatment after Poling on Dielectric and Piezoelectric Properties in Li0.06Na0.94NbO3 Ceramics

被引：8

作者：

Aoyagi, Rintaro ^{[1
]}

Maeda, Masaki ^{[1
]}

Yokota, Takeshi ^{[2
]}

Gomi, Manabu ^{[2
]}

机构：

[1] Nagoya Inst Technol, Grad Sch Engn, Dept Engn Phys Elect & Mech, Nagoya, Aichi 4668555, Japan

[2] Nagoya Inst Technol, Grad Sch Engn, Dept Mat Sci & Engn, Nagoya, Aichi 4668555, Japan

来源：

JAPANESE JOURNAL OF APPLIED PHYSICS | 2013年 / 52卷 / 09期

关键词：

LEAD-FREE; PHASE-TRANSITION; DEPOLARIZATION TEMPERATURE; ELECTRICAL-PROPERTIES; NIOBATE; FATIGUE;

D O I：

10.7567/JJAP.52.09KD12

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

The Influence of the heat treatment on the electrical properties in Li0.06Na0.94NbO3 (LNN6) lead-free ceramics was investigated. LNN6 poled samples showed an electromechanical coupling factor, k(p), of 0.19-0.20 and a mechanical quality factor, Q(m), of 800-900. By heat treatment at 320 degrees C for 10 h, k(p) hardly changed, but Q(m) markedly increased from 850 to 2890. The increase in Q(m) that depended on the heat treatment temperature and a higher Q(m) were obtained at 300 and 320 degrees C, which are near phase transition temperatures. The dielectric loss tan delta at a low frequency decreased with heat treatment. The poling field dependence of piezoelectric properties showed that the heat-treated samples have higher coercive field and internal bias. These results revealed that the heat treatment affects piezoelectric hardening for LNN6 ceramics. (C) 2013 The Japan Society of Applied Physics