UV-curable nanocasting technique to prepare bio-mimetic super-hydrophobic non-fluorinated polymeric surfaces for advanced anticorrosive coatings

被引：92

作者：

Peng, Chih-Wei ^{[1
,2
]}

Chang, Kung-Chin ^{[1
,2
]}

Weng, Chang-Jian ^{[1
,2
]}

Lai, Mei-Chun ^{[1
,2
]}

Hsu, Chien-Hua ^{[1
,2
]}

Hsu, Sheng-Chieh ^{[1
,2
]}

Li, Si-Ying ^{[1
,2
]}

Wei, Yen ^{[3
,4
]}

Yeh, Jui-Ming ^{[1
,2
]}

机构：

[1] Chung Yuan Christian Univ, Dept Chem, Chungli 32023, Taiwan

[2] Chung Yuan Christian Univ, Ctr Nanotechnol, Chungli 32023, Taiwan

[3] Tsinghua Univ, Dept Chem, Minist Educ, Beijing 100084, Peoples R China

[4] Tsinghua Univ, Minist Educ, Key Lab Organ Optoelect & Mol Engn, Beijing 100084, Peoples R China

来源：

POLYMER CHEMISTRY | 2013年 / 4卷 / 04期

关键词：

LOTUS; EPOXY; LEAF;

D O I：

10.1039/c2py20613g

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

In this study, a UV-curing nanocasting technique was first used to develop advanced anticorrosive coatings with bio-mimetic Xanthosoma sagittifolium leaf-like, non-fluorinated, super-hydrophobic polymeric surfaces. First of all, a transparent soft template with negative patterns of Xanthosoma sagittifolium leaf was fabricated by thermally curing the PDMS pre-polymer in molds at 60 degrees C for 4 h, followed by detaching the PDMS template from the surface of the natural leaf. Epoxy-acrylate coatings with biomimetic structures were prepared by performing the UV-radiation process after casting UV-curable precursor with photo-initiator onto a cold-rolled steel (CRS) electrode using the PDMS template. Subsequently, the UV-radiation process was carried out by using a light source with an intensity of 100 mW cm(2) with an exposing wavelength of 365 nm. The surface morphology of as-synthesized epoxy-acrylate coatings obtained from this UV-curing nanocasting technique was found to have lots of micro-scaled mastoids, each decorated with many nano-scaled wrinkles and was investigated systematically by scanning electron microscopy (SEM) and atomic force microscopy (AFM). It should be noted that the water contact angle (CA) of coating with bio-mimetic natural leaf surface was 153 degrees, which was found to significantly higher than that of the corresponding polymer with a smooth surface (i.e., CA = 81 degrees). The significant increase of the contact angle indicated that this bio-mimetic morphology exhibited effectively water-repelling properties, implying that it may be a potential candidate as advanced anticorrosive coating materials, which can be identified by series of electrochemical corrosion measurements. For example, it should be noted that the corrosion potential (E-corr) and corrosion current (I-corr), respectively, was found to shift from Ecorr = -730 mV and I-corr = 5.44 mu A cm(-2) of coating with smooth surface (SS) to E-corr = -394 mV and I-corr = 2.30 mu A cm(-2) of coating with biomimetic superhydrophobic surface (SPS).