Condensation energy density properties of Ba-122 pnictide superconductor with columnar defects introduced by heavy-ion irradiation

It is important to investigate condensation energy density of superconducting material, since it determines its pinning property. According to the heavy-ion irradiation, the columnar defects are introduced to the superconductor which act as the strong pinning centers, and the critical current density is enhanced by the new pinning centers. Since the number density and the size of the columnar defects can be observed, the condensation energy density is estimated by using the pinning summation theory. In the present study, we prepared Ba(Fe0.93Co0.07)(2)As-2(Ba-122) pnictide superconductors by self-flux method. 200 MeV Au ions were irradiated into the specimens along c-axis and the matching field was 2 T. After the irradiation, the critical current density was 6 times larger than that before the irradiation. The estimated condensation energy density is in the order of 10(4) J/m(3) and is slightly smaller than those of cuprate superconductors. The temperature dependence is similar to that of YBa2Cu3Ox oxide superconductors, since the anisotropy parameter is small in Ba-122. Therefore, it is expected to use Ba-122 at high temperatures near the critical temperature. (C) 2012 Published by Elsevier B. V. Selection and/or peer-review under responsibility of the Guest Editors.