EVALUATION OF THE STRUCTURAL CHANGES IN 9 % Cr CREEP-RESISTANT STEEL USING AN ELECTROCHEMICAL TECHNIQUE

被引：0

作者：

Rapouch, Jiri ^{[1
]}

Bystriansky, Jaroslav ^{[1
]}

Sefl, Vaclav ^{[1
]}

Svobodova, Marie ^{[1
]}

机构：

[1] Prague Inst Chem Technol, Dept Met & Corros Engn, CR-16628 Prague 6, Czech Republic

来源：

MATERIALI IN TEHNOLOGIJE | 2015年 / 49卷 / 04期

关键词：

9 % Cr creep-resistant steel; structural changes; electrochemical detection; polarization curve; MARTENSITIC STEELS; POLARIZATION; DEGRADATION;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A correct prediction of the remaining lifetime of the components for power plants requires an evaluation of the material structural stability. In this work, the possibility of a non-destructive evaluation of the structural changes in 9 % Cr creep-resistant steel P92 after a long-term annealing was investigated using the electrochemical-polarization technique. Aging at 650 degrees C caused a significant precipitation and coarsening processes resulting in a redistribution of some alloying elements in the structure. The structural changes confirmed by scanning-electron-microscopy observations and a hardness measurement affected the shape of the measured potentiodynamic curves. Significant local peaks on this curve, in the active-to-passive transition area and in the transpassive region, were evaluated. Characteristic current densities in these regions showed very good correlation with the results of the structure observation and hardness testing.

引用

页码：543 / 548

页数：6

共 50 条

[31] Design of a new 11Cr martensitic steel and evaluation of its long-term creep rupture strengths [J].

Dong, Z. ;

Chen, L. ;

Xiang, Z. D. .

JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 20 :3450-3455

[32] The Corrosion Behavior of 9Cr Ferritic-Martensitic Heat-Resistant Steel in Water and Chloride Environment [J].

Zhang, Z. ;

Singh, P. M. ;

Hu, Z. F. .

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2015, 137 (03)

[33] STUDY OF MECHANICAL DEGRADATION OF 9Cr-1Mo-V-Nb STEEL UNDER CREEP-FATIGUE INTERACTION CONDITIONS [J].

Kim, C. S. .

STRENGTH OF MATERIALS, 2017, 49 (01) :2-9

[34] Degradation Evaluation of Mechanical Property for Modified 9Cr-1Mo Steel by Reversible Permeability [J].

Bong, Chung-jong ;

Ryu, Kwon-sang ;

Nahm, Seung-hoon ;

Kim, Eun Kyu .

JOURNAL OF MAGNETICS, 2011, 16 (01) :42-45

[35] Study of Mechanical Degradation of 9Cr-1Mo-V-Nb Steel Under Creep-Fatigue Interaction Conditions [J].

C. S. Kim .

Strength of Materials, 2017, 49 :2-9

[36] Heterogeneous recovery and precipitation of Z phase during long term creep deformation of modified 9Cr-1Mo steel [J].

Suzuki, K ;

Kumai, S ;

Kushima, H ;

Kimura, K ;

Abe, F .

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2000, 86 (08) :550-557

[37] Comparative Evaluation of Creep-Rupture Behavior of P9 Steel Plate and Thick Section Tubeplate Forging [J].

Choudhary, B. K. ;

Isaac Samuel, E. ;

Christopher, J. ;

Yadav, S. D. .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (10) :6307-6319

[38] Degradation Evaluation of 1Cr-0.5Mo Steel using Barkhausen Noise [J].

Kim, Min-Gi ;

Park, Jong-Seo ;

Lee, Yun-Hee ;

Kim, CheolGi ;

Ryu, Kwon-Sang .

JOURNAL OF THE KOREAN MAGNETICS SOCIETY, 2011, 21 (04) :136-140

[39] Microstructural changes in steel 10Kh9V2MFBR during creep for 40000 hours at 600°C [J].

Fedoseeva, A. E. ;

Kozlov, P. A. ;

Dudko, V. A. ;

Skorobogatykh, V. N. ;

Shchenkova, I. A. ;

Kaibyshev, R. O. .

PHYSICS OF METALS AND METALLOGRAPHY, 2015, 116 (10) :1047-1056

[40] Plastic Limit Analysis of Modified 9Cr-1Mo Steel Pressure Vessel Containing Volume Defect with Creep Damage Law [J].

Du, Xianhe ;

Zhang, Jie ;

Peng, Heng ;

Liu, Yinghua .

INTERNATIONAL JOURNAL OF APPLIED MECHANICS, 2017, 9 (02)

← 1 2 3 4 5 →