Processing and compressive response of Al/SiC functionally graded composites

Compressive behavior of Al/SiC functionally graded composites (FGCs) was experimentally investigated. The FGC specimens are composed of ceramic (SiC) and metal (Al) constituent, varying in a predetermined configuration through the plate thickness. The compressive tests of FGCs manufactured with powder stacking hot-pressing technique were performed at different temperatures ranging from 25 to 150 degrees C. Al/SiC functionally graded composite specimens having three different compositions: n = 0.1, n = 0.5 and n = 1, were produced and compared to each other. It was found that the compression behavior of the FGCs was highly affected by composition variation through sample thickness. The strength of the composites decreased with the testing temperature. On the other hand, yield strength and ultimate compressive strength values increased with compositional gradient. The ultimate compressive strength of the composites reached 300 MPa. A minimum absorbed energy during the compressive tests was 25.2 x 10(-3) J/mm(3) and 96.9 x 10(-3) J/mm(3) for the test temperatures of 25 degrees C and 150 degrees C, respectively, for the compositional gradient n = 1. Graphic abstract