Magnetic and transport properties of amorphous Ce-Al alloy

Amorphous (a-) Ce50Al50 has been prepared by DC high-rate sputter method. The structure of the obtained sample has been confirmed to have an amorphous structure because there are no Bragg peaks in the X-ray diffraction measurement and have a clear exothermic peak by the differential scanning calorimetry measurement. We have measured the resistivity rho, magnetic susceptibility chi, specific heat C-p and thermoelectric power S for a-Ce50Al50. The temperature dependence of rho exhibits a small temperature dependence less than 10% in the whole temperature region. chi follows a Curie-Weiss behavior in the high-temperature region of T > 90 K. The effective paramagnetic moment p(eff), estimated from C is 2.18 mu(B)/Ce-atom. The low-temperature C-p/T increases rapidly with decreasing temperature and tends to a saturation. S(T) exhibits negative values in a wide temperature region. A minimum of S appear at around 60 K, and S decreases linearly with decreasing temperature down to 10 K. The low-temperature S is almost 0 mu V/K down to 2 K. From these results, we have pointed out that present a-Ce50Al50 would be an incoherent Kondo material.