Synthesis of effective poly(4-vinylpyridine) nanocomposites:: in situ polymerization from edges/surfaces and interlayer galleries of clay

Poly(4-vinylpyridine) (P4VP) nanocomposites have been prepared by using an in situ polymerization method in the presence of organically modified montmorillonite (MMT) clays with a quarternary salt of cocoamine containing a vinyl group, as well as trimethoxy vinyl silane. The nanocomposites were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and dynamic mechanical analysis (DMA). The desired exfoliated nanocomposite structure was achieved when the MMT modification was conducted in the presence of both modifiers, whereas individual modifications all resulted in intercalated structures. This resultant exfoliated nanocomposite was found to have better thermal stability and dynamic mechanical performance when compared to the other nanocomposites, even with 2 % clay loading. (c) 2005 Society of Chemical Industry.