Interface Reaction between Ceramic Moulds and High Nb-TiAl Alloys

被引：4

作者：

Lin Xiude ^{[1
]}

Xue Xiangyi ^{[1
]}

Zhong Hong ^{[1
]}

Zhang Tiebang ^{[1
]}

Li Jinshan ^{[1
]}

机构：

[1] Northwestern Polytech Univ, State Key Lab Solidificat Proc, Xian 710072, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2013年 / 42卷 / 08期

基金：

中国国家自然科学基金;

关键词：

high Nb-TiAl alloys; interface reaction; oxygen; microstructure transformation; MICROSTRUCTURE; OXYGEN;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The interface reaction between Ti-44Al-8Nb-0.2W-0.1B-0.1Y (at%) alloy and Al2O3/ZrO(2)JY(2)O(3) crucibles was investigated. The thicknesses of the interface reaction layers are about 40, 170 and 20 pin. The most interesting is the microstructure transformation of Ti-44Al-8Nb-0.2W-0.1B-0.1Y solidifying in different crucibles. After solidifying in Al2O3/ZrO2/Y2O3 crucibles, the oxygen contents in Ti-44Al-8Nb-0.2W-0.1B-0.1Y alloy are measured to be 0.35, 0.41 and 0.11 (at%). During melting and solidification, oxygen in crucibles will diffuse into the alloy matrix. High oxygen content causes microstructure transformation. Peritectic reaction occurs in the alloys solidifying in Al2O3 and ZrO2 crucibles. For contrast, Ti-49.5A1-2Cr-2Nb alloy was chosen to make investigation. No visible microstructure difference is found in alloys solidified in various crucibles though the oxygen contents are determined as 0.40, 0.63 and 0.25 (at%).

引用

页码：1568 / 1571

页数：4

共 17 条

[1]

Chevalier JP, 2005, MATER RES SOC SYMP P, V842, P145

[2] Directional solidification of Ti-45Al-8Nb-(W, B, Y) alloy [J].

Ding Xianfei ;

Lin Junpin ;

He Jianping ;

Ye Feng ;

Chen Guoliang .

RARE METALS, 2010, 29 (03) :292-297

[3] Induction melting of γ-TiAl in CaO crucibles [J].

Gomes, F. ;

Barbosa, Joaquim ;

Ribeiro, C. Silva .

INTERMETALLICS, 2008, 16 (11-12) :1292-1297

[4] The role of oxygen content and cooling rate on transformations in TiAl-based alloys [J].

Huang, A ;

Loretto, MH ;

Hu, D ;

Liu, K ;

Wu, XH .

INTERMETALLICS, 2006, 14 (07) :838-847

[5] A study of two refractories as mould materials for investment casting TiAl based alloys [J].

Jia, Q. ;

Cui, Y. Y. ;

Yang, R. .

JOURNAL OF MATERIALS SCIENCE, 2006, 41 (10) :3045-3049

[6] Investigation of interface reaction between TiAl alloys and mold materials [J].

Kim, MG ;

Kim, YJ .

METALS AND MATERIALS INTERNATIONAL, 2002, 8 (03) :289-293

[7] High temperature deformation behaviors of a high Nb containing TiAl alloy [J].

Lin, J. P. ;

Xu, X. J. ;

Wang, Y. L. ;

He, S. F. ;

Zhang, Y. ;

Song, X. P. ;

Chen, G. L. .

INTERMETALLICS, 2007, 15 (5-6) :668-674

[8] Microstructure and tensile properties of hot worked high Nb containing TiAl alloy on industrial scale [J].

Lin, JP ;

Xu, XJ ;

Gao, JF ;

Wang, YL ;

Lin, Z ;

Chen, GL .

PRICM 5: THE FIFTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-5, 2005, 475-479 :785-788

[9]

Lin KF, 1999, J AM CERAM SOC, V82, P3179

[10] Interfacial reactions between Ti-6Al-4V alloy and zirconia mold during casting [J].

Lin, KF ;

Lin, CC .

JOURNAL OF MATERIALS SCIENCE, 1999, 34 (23) :5899-5906

← 1 2 →