Tribological properties of Ni-Cr-W Matrix High Temperature Self-lubrication Composites Sintered by Hot Isostatic Pressing

被引：0

作者：

Sun, Jianrong ^{[2
]}

Li, Changsheng ^{[1
]}

Tang, Hua ^{[1
]}

Liu, Jinyinzi ^{[1
]}

Guo, Zhicheng ^{[1
]}

机构：

[1] Jiangsu Univ, Sch Mat Sci & Engn, Zhenjiang 212013, Peoples R China

[2] Jiangsu Univ, Sch Mech & Engn, Zhenjiang 212013, Peoples R China

来源：

HYDRAULIC EQUIPMENT AND SUPPORT SYSTEMS FOR MINING | 2013年 / 619卷

关键词：

High temperature; Self-lubrication; Powder metallurgy; Ni-W-Cr; HIP; ELEVATED-TEMPERATURES; WEAR; FILMS; WATER;

D O I：

10.4028/www.scientific.net/AMR.619.531

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The high temperature self-lubrication Ni-Cr-W matrix composites were prepared by powder metallurgy and sintered by hot isostatic pressing (HIP). Atomized Ni-Cr-W powder was mixed with friction components of MoS2 and Graphite. The mixed powders were cold pressed 450MPa and sintered at 1100 degrees C similar to 1200 degrees C in the presence of argon atmosphere for 1 hour under 180MPa hot isostatic pressing with respect to their application in slide bearing bushing. The tribological properties are investigated on UMT-2 tester in ball-on-disc against alloy steel ball. The results showed that the appropriate addition of MoS2 show excellent antifriction and wear resistance. And the friction coefficients and wear rates decrease over the wide temperature range of 25 degrees C similar to 600 degrees C compared that of the composites by pressureless sintered method. The results indicated that HIP technology had an obviously strengthening effect on the density, and anti-press strength.

引用

页码：531 / +

页数：2

共 16 条

[1] Lubrication of stellite at ambient and elevated temperatures by transfer films from a graphite slider [J].

Batchelor, AW ;

Lam, LN ;

Chandrasekaran, M .

WEAR, 1996, 198 (1-2) :208-215

[2]

DellaCorte C., 1990, NASA TECHNICAL MEMOR

[3] Effect of size refinement and distribution of lubricants on friction coefficient of high temperature self-lubricating composites [J].

Ding, Chun-Hua ;

Liu, Chun-Hui ;

Yang, Zhi-Mao ;

Wang, Ya-Ping ;

Sun, Zhan-Bo ;

Yu, Lie .

COMPOSITES SCIENCE AND TECHNOLOGY, 2010, 70 (06) :1000-1005

[4] Tribological evaluation on Ni3Al-based alloy and its composites under unlubricated wear condition [J].

Gong, Karin ;

Zhou, Zhifeng ;

Shum, P. W. ;

Luo, Heli ;

Tian, Zhiling ;

Li, Changhai .

WEAR, 2011, 270 (3-4) :195-203

[5]

Gongjun Cuilo z, TRIBINTD1100309

[6] The effectiveness of high temperature lubrication by in situ formation of graphite/MoS2 films [J].

Jin, YS ;

Zhou, CH .

WEAR, 1997, 205 (1-2) :77-87

[7] Wear performance of copper-graphite composite and a leaded copper alloy [J].

Kestursatya, M ;

Kim, JK ;

Rohatgi, PK .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 339 (1-2) :150-158

[8] Tribological properties of Ni3Al-Cr7C3 composite coating under water lubrication [J].

La, PQ ;

Xue, QJ ;

Liu, WM .

TRIBOLOGY INTERNATIONAL, 2000, 33 (07) :469-475

[9] Tribological properties of nickel-based self-lubricating composite at elevated temperature and counterface material selection [J].

Li, Jian Liang ;

Xiong, Dang Sheng .

WEAR, 2008, 265 (3-4) :533-539

[10]

Liu Ru-Tie, 2000, Journal of Central South University of Technology (Natural Science), V31, P260

← 1 2 →