Effect of Moisture Absorption on the Bending Fatigue Performance of Carbon/Epoxy Laminates

被引：0

作者：

Zhang, Aying ^{[1
,2
]}

Li, Dihong ^{[1
]}

Liang, Chengli ^{[3
]}

Jia, Jiusi ^{[4
]}

Zhang, Dongxing ^{[1
]}

机构：

[1] Harbin Inst Technol, Harbin 150001, Peoples R China

[2] Harbin Univ, Harbin 150086, Peoples R China

[3] Star Float Glass Co Ltd, Shenyang 110025, Peoples R China

[4] Sungkyunkwan Univ, Sch Mech Engn, Suwon 440746, South Korea

来源：

ADVANCED MATERIALS, PTS 1-3 | 2012年 / 415-417卷

关键词：

Carbon fiber; Laminates; Hygrothermal environment; Bending Fatigue; FRP COMPOSITES; BEHAVIOR; DURABILITY; DESIGN;

D O I：

10.4028/www.scientific.net/AMR.415-417.2308

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This study investigates the effect of moisture content on the bending fatigue properties of T300/914 composite laminates immersed in water for 7 days and 14 days. Displacement-controlled three-point bending fatigue tests were conducted on specimens. After 40,000 cycles the fatigue test was stopped and the properties were measured on the tested specimens. Reduction in material strength was found to depend on the level of moisture content. Experimental results reveal that the moisture content in the laminates increased with immersion time and that moisture absorption accelerated damage propagation in the composite. Hygrothermal ageing lowered the threshold level for the onset of fatigue. The experimental results were further validated by the supportive micrographs that illustrate different moisture content and their morphology before and after moisture absorption.

引用

页码：2308 / +

页数：2

共 50 条

[41] Evaluation of tensile properties in in-plane auxetic carbon/epoxy and carbon-glass/epoxy composite laminates
Veloso, Cristiano
Mota, Carlos
Cunha, Fernando
Sousa, Jose
Dias, Gustavo
Uribe, Braian
Fangueiro, Raul
JOURNAL OF COMPOSITE MATERIALS, 2025,
[42] The Thickness Effect of PSF Nanofibrous Mat on Fracture Toughness of Carbon/Epoxy Laminates
Saghafi, Hamed
Nikbakht, Ali
Mohammadi, Reza
Zarouchas, Dimitrios
MATERIALS, 2021, 14 (13)
[43] A multiaxial fatigue failure criterion based on the principal constant life diagrams for unidirectional carbon/epoxy laminates
Kawai, M.
Teranuma, T.
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2012, 43 (08) : 1252 - 1266
[44] Progressive matrix cracking in carbon/epoxy cross-ply laminates under static and fatigue loading
Llobet, J.
Maimi, P.
Essa, Y.
Martin de la Escalera, F.
INTERNATIONAL JOURNAL OF FATIGUE, 2019, 119 : 330 - 337
[45] Translaminar fracture toughness and fatigue crack growth characterization of carbon-epoxy plain weave laminates
Souza, Rafael R. R.
Nascimento Junior, Sergio L.
Silveira, Nubia N. A.
Arbelo, Mariano A.
Donadon, Mauricio V.
POLYMER COMPOSITES, 2019, 40 (10) : 3791 - 3804
[46] COMPRESSION FAILURE MODES OF CARBON FIBER FABRIC SCRAPS - EPOXY LAMINATES
Opelt, Carlos, V
Souza, Christiane S. R.
Marlet, Jose M. F.
Candido, Geraldo M.
Rezende, Mirabel C.
20TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS, 2015,
[47] Cyclic Olefin Copolymer Interleaves for Thermally Mendable Carbon/Epoxy Laminates
Zovi, Riccardo Costan
Mahmood, Haroon
Dorigato, Andrea
Fredi, Giulia
Pegoretti, Alessandro
MOLECULES, 2020, 25 (22):
[48] Effect of metal and polymer mating gears on the bending fatigue performance of asymmetric polymer gears
Pandian, A. Karthik
Gautam, Sachin Singh
Senthilvelan, S.
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART L-JOURNAL OF MATERIALS-DESIGN AND APPLICATIONS, 2021, 235 (10) : 2324 - 2339
[49] Strain amplitude controlled fatigue of Flax-epoxy laminates
Mahboob, Zia
Bougherara, Habiba
COMPOSITES PART B-ENGINEERING, 2020, 186
[50] Static and fatigue performance of graphene nanoplatelets coated bi-directional carbon fiber-epoxy composites under bending loads
Srivastava, Alok Kumar
Yerramalli, Chandra S.
Singh, Aparna
JOURNAL OF APPLIED POLYMER SCIENCE, 2024, 141 (33)

← 1 2 3 4 5 →