Evaluation of HIP pressure on Inconel 718 superalloy

被引:22
作者
Chang, S. H. [1 ]
Lee, S. C.
Tang, T. P.
Ho, H. H.
机构
[1] Natl Cheng Kung Univ, Dept Mat Sci & Engn, Tainan 701, Taiwan
[2] Natl Taipei Univ Technol, Dept Mat & Mineral Resources Engn, Taipei 106, Taiwan
[3] Chung Shan Inst Sci & Technol, Mat & Electroopt Res Div, Lungtan 325, Taiwan
关键词
hot isostatic pressing; Inconel; 718; superalloy; porosity; delta phase;
D O I
10.1179/136404606225023408
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
In the companion study 'Effects of temperature of HIP process on characteristics of Inconel 718 superalloy' in the present issue, the temperature parameters for hot isostatic pressing ( HIP) of Inconel 718 superalloy were discussed. That study showed that a HIP temperature of 1180 degrees C for Inconel 718 superalloy was optimum. The present study continues to discuss the effects of processing pressure of HIP for Inconel 718 superalloy. Four different HIP pressures were used: 1000, 1500, 1750 and 2000 bar (1 bar=0.0986 MPa). Meanwhile the HIP temperature was maintained at 1180 degrees C and soaking time was 2 h. To evaluate the effects of HIP pressure for Inconel 718 superalloy, tensile and bending tests at room and high temperature were evaluated. Porosity tests and microstructure inspection were also performed. The results show that 1750 bar of HIP treatment was optimum for Inconel 718 superalloy. It reduced the porosity by 78(.)5% and decreased the delta phase precipitation for Inconel 718 superalloy. It also increased the tensile strength by 18(.)48% at room temperature, 13(.)02% at 540 degrees C, and 20(.)11% at 650 degrees C. The elongation increased by 33(.)2% at room temperature, 124(.)82% at 540 degrees C, and 53(.)24% at 650 degrees C in tension tests. Finally, the results of three-point bending tests showed that the optimum processing pressure of HIP can enhance the bending strength by 32(.)45% at room temperature and 17(.)84% at 540 degrees C.
引用
收藏
页码:181 / 187
页数:7
相关论文
共 19 条
[1]  
*AM SOC MET, 1981, MAT HDB, V4
[2]  
ANTOLOVICH SD, 1992, SUPERALLOYS 1992, P23
[3]   Evaluation of fatigue crack growth rate and life prediction of Inconel 718 at room and elevated temperatures [J].
Chen, Q ;
Kawagoishi, N ;
Nisitani, H .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 277 (1-2) :250-257
[4]  
DONACHIE MJ, 1988, SUPERALLOYS TECHNICA, P47
[5]  
Durand-Charre M., 1997, MICROSTRUCTURE SUPER, P29
[6]  
Flow Autoclave System Inc, 1996, HOT IS PRESS APPL
[7]   Grain boundary niobium carbides in Inconel 718 [J].
Gao, M ;
Wei, RP .
SCRIPTA MATERIALIA, 1997, 37 (12) :1843-1849
[8]  
Garvare T., 1987, P INT C HOT IS PRESS, P3
[9]  
HAN X, 2003, J MATER PROCESS TECH, V137, P17
[10]  
KOIZUMI M, 1992, P 3 INT C HOT IS PRE, P195