Crystal structure solution for the A6B2O17 (A = Zr, Hf; B = Nb, Ta) superstructure

被引:71
作者
McCormack, Scott J. [1 ]
Kriven, Waltraud M. [1 ]
机构
[1] Univ Illinois, Dept Mat Sci & Engn, Urbana, IL 61801 USA
基金
美国国家科学基金会;
关键词
zirconium niobate Zr6Nb2O17; zirconium tantalate Zr6Nb2O17; hafnium niobate Hf6Nb2O17; hafnium tantalate Hf6Nb2O17; crystal structure solution; synchrotron X-ray powder diffraction; neutron powder diffraction; TANTALUM PENTOXIDE; THERMAL-EXPANSION; OXIDE ADDITIONS; DIFFRACTION; STABILIZATION; POLYMORPHISM; ATTENUATION; TABULATION; ZIRCONIA;
D O I
10.1107/S2052520619001963
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
Zr6Nb2O17, Hf6Nb2O17 and Hf6Nb2O17 crystal structure solutions have been solved using synchrotron X-ray powder diffraction and neutron powder diffraction in conjunction with simulated annealing, charge flipping and Rietveld refinement. These structures have been shown to be isomorphous with the Zr6Nb2O17 superstructure, leading to the classification of the A(6)B(2)O(17) (A = Zr, Hf; B = Nb, Ta) orthorhombic compound family with symmetry Ima2 (No. 46). The asymmetrical structural units of cation-centred oxygen polyhedra used to build the structure are as follows: (i) one set of symmetry-equivalent six-coordinated polyhedra, (ii) three sets of symmetry-equivalent seven-coordinated polyhedra and (iii) one set of symmetry-equivalent eight-coordinated polyhedra. The potential for cation order and disorder was discussed in terms of cation atomic number contrast in X-ray and neutron powder diffraction as well as the bond valence method. In addition, the structural mechanisms for experimentally observed compositional variations within the solid solution range can be attributed to the addition or removal of a set of symmetry-equivalent seven-coordinated polyhedra accompanied by corresponding oxygen tilts within the A(6)B(2)O(17 )structure.
引用
收藏
页码:227 / 234
页数:8
相关论文
共 41 条
[1]  
Brown I.D., 2006, The Chemical Bond in Inorganic Chemistry: The Bond Valence Model. International Union of Crystallography Monographs on Crystallography
[3]   THEORETICAL FORM-FACTOR, ATTENUATION AND SCATTERING TABULATION FOR Z=1-92 FROM E=1-10 EV TO E=0.4-1.0 MEV [J].
CHANTLER, CT .
JOURNAL OF PHYSICAL AND CHEMICAL REFERENCE DATA, 1995, 24 (01) :71-591
[4]   CRYSTAL-STRUCTURE DETERMINATION BY POWDER NEUTRON-DIFFRACTION AT THE SPALLATION NEUTRON SOURCE, ISIS [J].
CHEETHAM, AK ;
DAVID, WIF ;
EDDY, MM ;
JAKEMAN, RJB ;
JOHNSON, MW ;
TORARDI, CC .
NATURE, 1986, 320 (6057) :46-48
[5]   FRAMEWORK CRYSTAL-STRUCTURE SOLUTION BY SIMULATED ANNEALING - TEST APPLICATION TO KNOWN ZEOLITE STRUCTURES [J].
DEEM, MW ;
NEWSAM, JM .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1992, 114 (18) :7189-7198
[6]   A simulated annealing approach for crystal structure solution from powder diffraction data [J].
Engel, GE ;
Wilke, S ;
Harris, KDM ;
Kariuki, BM ;
Ahn, S ;
Leusen, FJJ ;
Neumann, MA .
MOLECULAR CRYSTALS AND LIQUID CRYSTALS, 2001, 356 :355-364
[7]   FOX, 'free objects for crystallography':: a modular approach to ab initio structure determination from powder diffraction [J].
Favre-Nicolin, V ;
Cerny, R .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2002, 35 :734-743
[8]   Stabilization of the high-k tetragonal phase in HfO2: The influence of dopants and temperature from ab initio simulations [J].
Fischer, Dominik ;
Kersch, Alfred .
JOURNAL OF APPLIED PHYSICS, 2008, 104 (08)
[9]   CRYSTAL-STRUCTURE OF NB2ZR6O17 [J].
GALY, J ;
ROTH, RS .
JOURNAL OF SOLID STATE CHEMISTRY, 1973, 7 (03) :277-285
[10]  
Gulgun MA., 2002, Patent No. [6482387 B1, 6482387]