Effect of bond coat surface roughness on oxidation behaviour of air plasma sprayed thermal barrier coatings

被引：25
作者：
Che, C. [1 ]
Wu, G. Q. [1 ]
Qi, H. Y. [2 ]
Huang, Z. [1 ]
Yang, X. G. [2 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
[2] Beijing Univ Aeronaut & Astronaut, Sch Jet Prop, Beijing 100083, Peoples R China
来源：
SURFACE ENGINEERING | 2008年 / 24卷 / 04期
关键词：
thermal barrier coating; MCrAIY; oxidation; roughness; lifetime; failure;
D O I：
10.1179/026708408X329470
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Two layered thermal barrier coatings (TBCs) with different bond coat surface roughnesses were produced by air plasma spraying. Isothermal oxidation test was carried out to evaluate the durability and oxidation behaviour of these systems. The results show that the roughness of bond coat significantly affects the lifetime of TBCs. With the increase in bond coat roughness, the lifetime decreases exponentially. The durability is enhanced by surface grinding treatments that decrease diffusion paths on the surface of the bond coat and diminish Al depletion rate. The shape and path of cracks at failure are also affected by the bond coat surface roughness.
引用
收藏
页码：276 / 279
页数：4
相关论文
共 16 条
  • [1] A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system. Part II: Life prediction model
    Busso, EP
    Lin, J
    Sakurai, S
    [J]. ACTA MATERIALIA, 2001, 49 (09) : 1529 - 1536
  • [2] Interfacial damage in EB-PVD thermal barrier coatings due to thermal cycling
    Chaudhury, ZA
    Newaz, GM
    Nusier, SQ
    Ahmed, T
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 231 (1-2): : 34 - 41
  • [3] The growth and influence of thermally grown oxide in a thermal barrier coating
    Chen, W. R.
    Wu, X.
    Marple, B. R.
    Patnaik, P. C.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2006, 201 (3-4) : 1074 - 1079
  • [4] ON THE MECHANICAL-BEHAVIOR OF BRITTLE COATINGS AND LAYERS
    EVANS, AG
    CRUMLEY, GB
    DEMARAY, RE
    [J]. OXIDATION OF METALS, 1983, 20 (5-6): : 193 - 216
  • [5] Diffusion cells and chemical failure of MCrAlY bond coats in thermal-barrier coating systems
    Evans, HE
    Taylor, MP
    [J]. OXIDATION OF METALS, 2001, 55 (1-2): : 17 - 34
  • [6] Haynes JA, 1996, SURF COAT TECH, V86, P102, DOI 10.1016/S0257-8972(96)02985-4
  • [7] Potential influences of bond coat impurities and void growth on premature failure of EB-PVD TBCs
    Haynes, JA
    [J]. SCRIPTA MATERIALIA, 2001, 44 (07) : 1147 - 1152
  • [8] MAO WG, 2000, SURF COAT TECH, V133, P28
  • [9] INTERFACE STABILITY IN THE NI-CR-AL SYSTEM .1. MORPHOLOGICAL STABILITY OF BETA-GAMMA DIFFUSION COUPLE INTERFACES AT 1150-DEGREES-C
    MERCHANT, SM
    NOTIS, MR
    GOLDSTEIN, JI
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (07): : 1901 - 1940
  • [10] PREDICTING DIFFUSION PATHS AND INTERFACE MOTION IN GAMMA-GAMMA+BETA, NI-CR-AL DIFFUSION COUPLES
    NESBITT, JA
    HECKEL, RW
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (12): : 2087 - 2094
12