Mesoporous γ-alumina synthesized by hydro-carboxylic acid as structure-directing agent

被引:96
|
作者
Liu, Qian
Wang, Aiqin
Wang, Xiaodong
Zhang, Tao
机构
[1] Chinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China
[2] Grad Univ, Chinese Acad Sci, Beijing, Peoples R China
基金
中国国家自然科学基金;
关键词
mesoporous alumina; gamma-alumina; mesoporous material; non-surfactant template; hydro-carboxylic acid;
D O I
10.1016/j.micromeso.2005.12.012
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
A facile and non-surfactant-templating route is described for preparing mesoporous gamma-aluminas with improved textural properties. In this synthesis, hydro-carboxylic acid (HCA) was used as the structure-directing agent and boehmite sol as the precursor. By drying the mixture of HCA and boehmite sol at a suitable temperature and then calcining at 773 K, the mesoporous gamma-alumina with controllable pore structures could be obtained. The drying temperature of the initial boehmite-HCA mixture had an important effect on the pore structure of the final product. As the drying temperature increased successively from 303 K to 373 K and 423 K, the products changed correspondingly from a bimodal mesoporous structure to a uniform mesostructure and a micro-mesoporous structure. By means of various characterization techniques, including N-2 physical adsorption, TEM, SEM, XRD Al-27 NMR, FTIR and TG-DTA, it was demonstrated that the coordination between HCA and aluminum became stronger with the increase of the drying temperature, so that the strong coordination interaction between the HCA and the boehmite colloid particulates could induce a kind of arrangement of rigid boehmite "building blocks", thus giving rise to different pore structures. (c) 2006 Elsevier Inc. All rights reserved.
引用
收藏
页码:10 / 21
页数:12
相关论文
共 50 条
  • [1] Synthesis of texture-excellent mesoporous alumina using PEG1000 as structure-directing agent
    Kui Zhang
    Changming Li
    Jian Yu
    Shiqiu Gao
    Guangwen Xu
    Chinese Journal of Chemical Engineering, 2017, 25 (01) : 137 - 141
  • [2] Synthesis of texture-excellent mesoporous alumina using PEG1000 as structure-directing agent
    Zhang, Kui
    Li, Changming
    Yu, Jian
    Gao, Shiqiu
    Xu, Guangwen
    CHINESE JOURNAL OF CHEMICAL ENGINEERING, 2017, 25 (01) : 137 - 141
  • [3] Transparent monolithic cubic mesoporous silica synthesized by structure-directing surfactant
    C.P. Singh
    M. Yousuf
    S.B. Qadri
    D.C. Turner
    B.P. Gaber
    B.R. Ratna
    Applied Physics A, 2003, 77 : 585 - 589
  • [4] Transparent monolithic cubic mesoporous silica synthesized by structure-directing surfactant
    Singh, CP
    Yousuf, M
    Qadri, SB
    Turner, DC
    Gaber, BP
    Ratna, BR
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2003, 77 (3-4): : 585 - 589
  • [5] Effect of nonionic structure-directing agents on adsorption and structural properties of mesoporous alumina
    Cai, Weiquan
    Yu, Jiaguo
    Jaroniec, Mietek
    JOURNAL OF MATERIALS CHEMISTRY, 2011, 21 (25) : 9066 - 9072
  • [6] Mesoporous titania with anatase framework synthesized using polyphenolic structure-directing agent: Synthesis domain and catalytic metal loading
    Shin, Hye Sun
    Jo, Changbum
    Ko, Seung Hyeon
    Ryoo, Ryong
    MICROPOROUS AND MESOPOROUS MATERIALS, 2015, 212 : 117 - 124
  • [7] Influence of structure-directing agent on zeolite synthesis
    Suzuki, A
    Wang, ZB
    Ahn, CH
    Sano, T
    Soga, K
    NIPPON KAGAKU KAISHI, 1999, (07) : 487 - 491
  • [8] Synthesis of highly ordered mesoporous silica using cationic trimeric surfactant as structure-directing agent
    Yan, Xin
    Han, Shuhua
    Hou, Wanguo
    Yu, Xiaojuan
    Zeng, Chunmei
    Zhao, Xiaohong
    Che, Hongwei
    COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2007, 303 (03) : 219 - 225
  • [9] Mesoporous hybrid zirconium oxophenylphosphate synthesized in absence of any structure directing agent
    Sarkar, Krishanu
    Yokoi, Toshiyuki
    Tatsumi, Takashi
    Bhaumik, Asim
    MICROPOROUS AND MESOPOROUS MATERIALS, 2008, 110 (2-3) : 405 - 412
  • [10] Nano-architecture by molecular structure-directing agent
    Xia, Hai-Bing
    Liu, Xiang-Yang
    Zhang, Ke-Qin
    CHEMISTRY OF MATERIALS, 2008, 20 (07) : 2432 - 2434