Fretting wear behavior of PVD TiB2 coatings

被引：26
作者：
Prakash, B
Ftikos, C
Celis, JP
机构：
[1] Katholieke Univ Leuven, Dept Met & Toegepaste Mat, B-3001 Louvain, Belgium
[2] Natl Tech Univ Athens, Dept Chem Engn, GR-15773 Athens, Greece
来源：
SURFACE & COATINGS TECHNOLOGY | 2002年 / 154卷 / 2-3期
关键词：
titanium diboride; sputtering; magnetron; wear;
D O I：
10.1016/S0257-8972(02)00035-X
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
TiB2 coatings deposited on hardened high-speed steel by magnetron sputtering were tested for their friction and wear behavior. Fretting wear tests (mode 1) were carried out on as-deposited coatings, and after annealing in air at 600 degreesC for 1 h. The as deposited magnetron sputtered TiB2 coating shows a better wear resistance (2000 mum(3)/J) than a hard TiN coating. On the contrary, the annealed TiB2 coating shows a low wear resistance (14 000 mum(3)/J) due to intensive cracking and oxidation. However, a low coefficient of friction was not noticed with neither as-deposited nor annealed TiB, coatings. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：182 / 188
页数：7
相关论文
共 27 条
[1]   RUTILE - NORMAL PROBABILITY PLOT ANALYSIS AND ACCURATE MEASUREMENT OF CRYSTAL STRUCTURE [J].
ABRAHAMS, SC ;
BERNSTEI.JL .
JOURNAL OF CHEMICAL PHYSICS, 1971, 55 (07) :3206-&
[2]  
AGARWAL A, 2000, J MAT, V52, P14
[3]   Fretting wear behavior of TiB2-based materials against bearing steel under water and oil lubrication [J].
Basu, B ;
Vleugels, J ;
Van der Biest, O .
WEAR, 2001, 250 :631-641
[4]  
Blanpain B., 1994, Diamond Films and Technology, V3, P177
[5]   FRETTING WEAR OF SELECTED CERAMICS AND CERMETS [J].
CAMPBELL, PQ ;
CELIS, JP ;
ROOS, JR ;
VANDERBIEST, O .
WEAR, 1994, 174 (1-2) :47-56
[6]  
Celis JP, 1998, SURFACE MODIFICATION TECHNOLOGIES XI, P860
[7]   OPTIMIZATION AND CHARACTERIZATION OF LPCVD TIB2 FOR ULSI APPLICATIONS [J].
CHOI, CS ;
RUGGLES, GA ;
OSBURN, CM ;
XING, GC .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1991, 138 (10) :3053-3061
[8]   Preparation of ultralow-friction surface films on vanadium diboride [J].
Erdemir, A ;
Halter, M ;
Fenske, GR .
WEAR, 1997, 205 (1-2) :236-239
[9]   Tribology of naturally occurring boric acid films on boron carbide [J].
Erdemir, A ;
Bindal, C ;
Zuiker, C ;
Savrun, E .
SURFACE & COATINGS TECHNOLOGY, 1996, 86-7 (1-3) :507-510
[10]  
Erdemir A, 1995, SURF COAT TECH, V76-77, P443
123