Submerged Friction Stir Welding of 2024-T4 Aluminum Alloy

被引：0

作者：

Wang Kuaishe ^{[1
]}

Wu Nan ^{[1
]}

Wang Wen ^{[1
]}

Ding Kai ^{[1
]}

Guo Qiang ^{[1
]}

机构：

[1] Xian Univ Architecture & Technol, Xian 710055, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2013年 / 42卷 / 09期

关键词：

aluminum alloy; friction stir welding; cooling water medium; microstructure; mechanical properties; MECHANICAL-PROPERTIES; BEHAVIOR;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

2024-T4 aluminum alloy plate was jointed by friction stir welding (FSW) under air and cooling water circulation separately, and the effect of the cooling water on the microstructure and mechanical properties of the FSW joint was investigated. The results show that the cooling water circulation medium has a significant instantaneous cooling effect. Cooling water causes remarkable grain refinement with an average grain size of 700 nm in the nugget zone. The growth of precipitates is restrained by cooling water, and the size of precipitates is 30 similar to 200 nm in the nugget zone. Cooling water decreases the thermal softening effect on the FSW joint, thus improving the microstructure and properties of the joint. HV microhardness and tensile strength of SFSW joint are increased by 234 MPa and 52.2 MPa, respectively, but the elongation is decreased a little.

引用

页码：1949 / 1952

页数：4

共 10 条

[1] Influence of the initial ageing condition on microstructure and properties of a Friction Stir Welded 6056 alloy [J].

Denquin, A ;

Allehaux, D ;

Campagnac, MH ;

Lapasset, G .

ALUMINUM ALLOYS 2002: THEIR PHYSICAL AND MECHANICAL PROPERTIES PTS 1-3, 2002, 396-4 :1199-1204

[2] Quantitative investigation of precipitation and mechanical behaviour for AA2024 friction stir welds [J].

Genevois, C ;

Deschamps, A ;

Denquin, A ;

Doisneau-cottignies, B .

ACTA MATERIALIA, 2005, 53 (08) :2447-2458

[3] The effect of welding parameters on the corrosion behaviour of friction stir welded AA2024-T351 [J].

Jariyaboon, M. ;

Davenport, A. J. ;

Ambat, R. ;

Connolly, B. J. ;

Williams, S. W. ;

Price, D. A. .

CORROSION SCIENCE, 2007, 49 (02) :877-909

[4] The improvement of mechanical properties of friction-stir-welded A356 Al alloy [J].

Lee, WB ;

Yeon, YM ;

Jung, SB .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 355 (1-2) :154-159

[5] Effect of welding speed on microstructures and mechanical properties of underwater friction stir welded 2219 aluminum alloy [J].

Liu, H. J. ;

Zhang, H. J. ;

Yu, L. .

MATERIALS & DESIGN, 2011, 32 (03) :1548-1553

[6] Tensile properties and fracture locations of friction-stir-welded joints of 2017-T351 aluminum alloy [J].

Liu, HJ ;

Fujii, H ;

Maeda, M ;

Nogi, K .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 142 (03) :692-696

[7] Mechanical properties of underwater friction stir welded 2219 aluminum alloy [J].

Liu Hui-jie ;

Zhang Hui-jie ;

Huang Yong-xian ;

Yu Lei .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2010, 20 (08) :1387-1391

[8] Friction stir welding and processing [J].

Mishra, RS ;

Ma, ZY .

MATERIALS SCIENCE & ENGINEERING R-REPORTS, 2005, 50 (1-2) :1-78

[9] Corrosion-fatigue crack growth in friction stir welded Al 7050 [J].

Pao, PS ;

Gill, SJ ;

Feng, CR ;

Sankaran, KK .

SCRIPTA MATERIALIA, 2001, 45 (05) :605-612

[10]

Thomas WM, 1991, GB patent, Patent No. [91259788, PCT/GB92]

← 1 →