Evaluation of Al2O3 MOCVD Coating for Titanium Alloys Protection Under Severe Conditions At High Temperature

被引：4

作者：

Beguin, J. D.

Samelor, D. ^{[1
]}

Vahlas, C. ^{[1
]}

Gleizes, A. ^{[1
]}

Petit, J. A.

Sheldon, B. ^{[2
]}

机构：

[1] ENSIACET, CIRIMAT CNRS, F-31077 Toulouse 4, France

[2] Brown Univ, Providence, RI 02912 USA

来源：

HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2 | 2008年 / 595-598卷

关键词：

MOCVD; Al(2)O(3) coating; NaCl-induced corrosion; corrosion protection;

D O I：

10.4028/www.scientific.net/MSF.595-598.719

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The corrosion resistance of MOCVD Al(2)O(3) coating system was investigated to protect a TA6V Alloy under hot salt corrosion conditions: This coating was corroded with a salt deposit without mechanical loading at 480 degrees C during 100 h. Corrosion products formed in salted areas were studied by Energy Dispersive Spectroscopy (EDS). Although all coated specimens were damaged with corrosion products presence in salted area, Al(2)O(3) coatings showed the lowest salt damage on titanium substrate after a metallographic cross section observation compared to uncoated ones. As well as these interesting experimental results, coated specimens exhibit a good adherence on titanium substrate