Preparation and luminescence properties of SiO2@LaBO3:Eu3+ nanoparticles

Spherical SiO2 particles having a LaBO3:Eu3+ shell have been prepared by coating of silica nanoparticles (size around 130-150 nm) with a LaBO3:Eu3+ sol-gel precursor and subsequent calcination. The SiO2@LaBO3:Eu3+ nanoparticles were characterized by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy, and transmission electron microscopy. The XRD and FTIR results revealed that the LaBO3:Eu3+ layer on SiO2 nanoparticles formed an H-LaBO3 crystal phase when calcination at a temperature up to 700 degrees C. Both excitation and emission properties were characterized. The strong excitation lines at 393 and 465 nm of SiO2@LaBO3:Eu3+ indicated that the core-shell phosphor matched well with the output wavelength of near-UV (350-400 nm) or blue LED (450 nm) chips in phosphor-converted W-LEDs. The emission spectra of the D-5(0) -> F-7(J) (J = 0, 1, 2, 3, and 4) transitions at blue/near-UV light showed strong emission lines around 615 nm which were attributed to the induced electric dipole transition of D-5(0) -> F-7(2). The coating cycles affected the luminescence of SiO2@LaBO3:Eu3+ nanoparticles and their CIE chromaticity coordinate shifted from orange-red to the deep red zone with the increase in the coating cycles (up to 3). The luminescence lifetime of the Eu3+ ions in SiO2@LaBO3:Eu3+ was 2.32 ms. Such a luminescent material may be useful for display and light applications.